Composite material including a thermoplastic polymer, a pest food material, and a pesticide

ABSTRACT

Composite materials that are palatable to a wood-destroying pest species and also pesticidal to the pest species can be used in pest control devices and can be used as wood substitutes for structural components, which are resistant to destruction by wood-destroying pests. The composite materials include a thermoplastic polymer, a food material for the pest and a pesticide. The composite material is formed by mixing a thermoplastic polymer, wood fragments or other cellulosic materials and a quantity of pesticide, and thereafter creating a molten material within a mixer, compounder, extruder or the like. The molten material is extruded or molded to form the desired shape.

CROSS-REFERENCE TO RELATED APPLICATIONS

The present application is a continuation of U.S. patent applicationSer. No. 15/691,186, filed 30 Aug. 2017, which is a continuation of U.S.patent application Ser. No. 14/790,691, filed 2 Jul. 2015, which is acontinuation of U.S. patent application Ser. No. 12/004,655, filed 21Dec. 2007, now U.S. Pat. No. 9,101,124, which claims the benefit of U.S.Provisional Patent Application No. 60/876,351, filed 21 Dec. 2006, eachof which is incorporated herein by reference in its entirety

BACKGROUND

The present application relates to composite materials that arepalatable to a wood-destroying pest species and also pesticidal to thepest species. More particularly, but not exclusively, the applicationrelates to composite materials composed of a thermoplastic polymer, afood material for the pest and a pesticide.

The protection of wooden structures from damage caused by pests has beenan area of particular interest for many years, and the removal of pestsfrom areas occupied by humans, livestock, and crops has long been achallenge. Pests of frequent concern include various types of insectsand rodents. Subterranean termites are a particularly troublesome typeof pest with the potential to cause severe damage to wooden structures.Various schemes have been proposed to eliminate termites and certainother harmful pests of both the insect and noninsect variety. In oneapproach, pest control relies on the blanket application of chemicalpesticides in the area to be protected. However, as a result ofenvironmental regulations, this approach is becoming less desirable.

Recently, advances have been made to provide for the targeted deliveryof pesticide chemicals. U.S. Pat. No. 5,815,090 to Su is one example.Another example directed to termite control is the SENTRICON® TermiteColony Elimination System of Dow AgroSciences LLC that has a businessaddress of 9330 Zionsville Road, Indianapolis, Ind. In this system, anumber of units each having a termite edible material, are placed atleast partially in the ground about a dwelling to be protected. Theunits are inspected routinely by a pest control service for the presenceof termites, and inspection data is recorded with reference to a uniquebarcode label associated with each unit. If termites are found in agiven unit, a bait is installed that contains a slow-acting pesticideintended to be carried back to the termite nest to eradicate the colony.There is a continuing demand for further advancement in the areas ofpest control, pest-resistant structural materials and relatedtechnologies, and the development of new techniques for more reliablyand/or cost-effectively preventing damage to wooden structures anderadicating termites or other pests are desired.

SUMMARY

In one aspect, the present application provides a pest control devicethat includes a bait operable to be consumed or displaced by one or morespecies of pest and a housing at least partially enclosing the bait. Thebait includes a composite material including a plastic structuralmatrix, a cellulosic food material contained within the matrix that ispalatable to the pest and a pesticide contained within the matrix thatis toxic to the pest.

In another aspect, the application provides a pest control system thatincludes at least two pest control devices each arranged to be spacedapart from one another in an area to be protected from one or morepests. At least one of the pest control devices includes a bait that isoperable to be consumed or displaced by the pest and that includes acomposite material including a plastic structural matrix, a cellulosicfood material contained within the matrix that is palatable to the pestand a pesticide contained within the matrix that is toxic to the pest.

In yet another aspect, the application provides a method that includes:(1) providing a pest control device including a pesticidal bait for oneor more species of pest; and (2) installing the device in an area to beprotected from the pests. The pesticidal bait includes a compositematerial including a plastic structural matrix, a cellulosic foodmaterial contained within the matrix that is palatable to the pest and apesticide contained within the matrix that is toxic to the pest.

In still another aspect, the application provides a method for making acomposite material that includes: (1) providing a mixture of a softenedor molten thermoplastic polymer having a softening or melting pointbelow about 220° C., a cellulosic food material that is palatable to atleast one species of wood-destroying pest and a pesticide that is toxicto the pest; (2) forming the mixture to provide a workpiece having adesired shape; and (3) cooling the workpiece to a temperature below thesoftening or melting point of the plastic to provide a solid compositearticle. As used herein, the term “molten” is intended to refer to astate of a thermoplastic polymer in which the polymer is fully melted,partially melted, or sufficiently softened or tacky that the polymer canbe formed, for example by extrusion or molding and then cooling, into aplastic matrix. Similarly, the term “melting point” as used herein isintended to refer to the temperature at which a given polymer or mixtureof polymers melts, softens or becomes tacky, and encompasses the glasstransition temperature for amorphous polymers. A person skilled in theart will appreciate that the melting point of a given polymer or mixtureof polymers can be modified by contacting the polymer or mixture ofpolymers with certain solvents and/or other additives. In oneembodiment, the mixture is formed by extrusion.

In another aspect of the present application, there is provided acomposite material that includes a plastic structural matrix, acellulosic food material contained within the matrix that is palatableto at least one species of wood-destroying pest and a pesticidecontained within the matrix that is toxic to the pest. The compositematerial is operable to be consumed or displaced by the pest; and theplastic structural matrix comprises a thermoplastic polymer having amelting point below about 220° C.

Also provided by the present application is a composite material thatincludes a plastic structural matrix, a cellulosic food materialcontained within the matrix that is palatable to at least one species ofwood-destroying pest and a pesticide contained within the matrix that istoxic to the pest; in which the composite material is operable to beconsumed or displaced by the pest, and the plastic structural matrixcomprises a thermoplastic polymer that includes a thermoplasticcellulose derivative.

In yet another aspect of the present application, there is provided acomposite material that includes a rigid plastic structural matrixcomprising a thermoplastic polymer, a cellulosic food material containedwithin the matrix that is palatable to at least one species ofwood-destroying pest and a pesticide contained within the matrix that istoxic to the pest, in which the composite material is operable to beconsumed or displaced by the pest.

In still another aspect of the application, there is provided anextruded wood substitute material that includes a composite materialincluding a plastic structural matrix, a cellulosic food materialcontained within the matrix that is palatable to the pest and apesticide contained within the matrix that is toxic to the pest.

Further embodiments, forms, features and aspects of the presentapplication shall become apparent from the detailed description andfigures provided herewith.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a diagrammatic view of a pest control system that includesseveral pest control device.

FIG. 2 is a view of selected elements of the system of FIG. 1 inoperation.

FIG. 3 is an exploded, partial sectional view of a pest monitoringassembly of one embodiment of pest control device.

FIG. 4 is an exploded, partial sectional view of the pest monitoringassembly of FIG. 3 along a view plane perpendicular to the view plane ofFIG. 3.

FIG. 5 is a partial, top view of a portion of a communication circuitsubassembly of the pest monitoring assembly shown in FIGS. 3 and 4.

FIG. 6 is an exploded assembly view of the pest control device with thepest monitoring assembly of FIG. 3.

FIG. 7 is an exploded assembly view of the pest control device with apesticide delivery assembly in place of the pest monitoring assembly ofFIG. 3.

FIG. 8 is a schematic representation of a first test set-up as describedin the Examples.

FIG. 9 is a schematic representation of a second test set-up asdescribed in the Examples.

FIG. 10 is a chart depicting survivorship data from the experimentreported in Example 7.

FIG. 11 is a chart depicting survivorship data from the experimentreported in Example 7.

FIG. 12 is a chart depicting survivorship data from the experimentreported in Example 7.

FIG. 13 is a chart depicting survivorship data from the experimentreported in Example 7.

FIG. 14 is a chart depicting survivorship data from the experimentreported in Example 7.

FIG. 15 is a chart depicting survivorship data from the experimentreported in Example 7.

FIG. 16 is a chart depicting survivorship data from the experimentreported in Example 7.

FIG. 17 is a chart depicting survivorship data from the experimentreported in Example 7.

FIG. 18 is a chart depicting survivorship data from the experimentreported in Example 7.

FIG. 19 is a chart depicting survivorship data from the experimentreported in Example 7.

FIG. 20 is a chart depicting survivorship data from the experimentreported in Example 7.

FIG. 21 is a chart depicting survivorship data from the experimentreported in Example 7.

FIG. 22 is a chart depicting trophallaxis transfer survivorship datafrom the experiment reported in Example 8.

FIG. 23 is a chart depicting trophallaxis transfer survivorship datafrom the experiment reported in Example 8.

FIG. 24 is a chart depicting trophallaxis transfer survivorship datafrom the experiment reported in Example 8.

FIG. 25 is a chart depicting trophallaxis transfer survivorship datafrom the experiment reported in Example 8.

FIG. 26 is a chart depicting consumption data from the experimentreported in Example 9.

FIG. 27 is a chart depicting survivorship data from the experimentreported in Example 9.

FIG. 28 is a chart depicting survivorship data from the experimentreported in Example 9.

FIG. 29 is a chart depicting mean days to elimination data from theexperiment reported in Example 10.

FIG. 30 is a chart depicting consumption data from the experimentreported in Example 10.

FIG. 31 is a chart depicting consumption data from the experimentreported in Example 10.

DETAILED DESCRIPTION OF SELECTED EMBODIMENTS

For the purposes of promoting an understanding of the principles of theinventions described herein, reference will now be made to theembodiments illustrated in the drawings and specific language will beused to describe the same. It will nevertheless be understood that nolimitation of the scope of any invention is thereby intended. Anyalterations and further modifications in the illustrated embodiments,and any further applications of the principles described and illustratedherein are contemplated as would normally occur to one skilled in theart.

Composite materials that can be used to deliver pesticides towood-destroying pests include a plastic structural matrix, a cellulosicfood material palatable to at least one species of wood-destroying pestand a pesticide that is toxic to the pest. The term “wood-destroyingpest” is used herein to refer to an insect or other pest that destroysthe structural integrity of wood by boring into wood or consuming wood.Examples include, without limitation, termites, carpenter ants,carpenter wasps and other wood boring or cellulose consuming organisms.Making the composite materials described herein does not requirematerial processing at high temperatures that would destroy thefunctionality of the pesticide. The term “pesticide” is used herein torefer to a compound that is toxic to at least one target species ofwood-destroying pests. The plastic structural matrix of the composite iscomposed of a thermoplastic polymer processed into a form that providessufficient strength and structural integrity for a desired end use ofthe composite material. The pesticide retains its bioactivity as itresides within the composite, and produces a desired result after thematerial is ingested by or otherwise comes into contact with pests.Polymeric materials included in the composite materials can be processedusing relatively low-temperature extrusion or molding processes andprovide composite material articles with structural integrity, with goodacceptance by target wood-destroying pests (i.e., palatability to targetwood-destroying pests), and without nullifying the functionality ofpesticides processed therewith, which can include temperature sensitivepesticides. In one embodiment, the plastic structural matrix of thecomposite material is rigid.

In one embodiment, the cellulosic food material is selected based uponknown or measured attractability for a given pest that is beingtargeted. For example, when a composite material is to be used as a baitfor a certain target pest species, the composite material can be madeusing a cellulosic food material that is a favorite food of the targetpest species. The cellulosic food material would therefore attractmembers of the target pest species and would be expected to be consumedor displaced by the pests, which would result in the simultaneousconsumption or displacement of the pesticide present in the compositematerial, producing a desired pesticidal effect. The food material canbe composed in whole or in part by an edible plastic material.Alternatively, the food material can be composed in whole or in part bya non-plastic cellulosic material. In one embodiment, the food materialis a purified cellulose, such as, for example, alpha cellulose, betacellulose or gamma cellulose. One suitable example is preferred texturecellulose (PTC). In another embodiment, the food material is wood or aderivative of wood, such as, for example, wood chips, wood fibers,sawdust, cardboard, paper or other material that is palatable to atarget wood-destroying species. Other cellulosic food materials that canbe employed include microcrystalline cellulose, examples of which areprovided in U.S. Pat. No. 6,416,752, which is incorporated herein byreference, and modified polymeric cellulose based materials such as, forexample, METHOCEL® or ETHOCEL®, which are available commercially fromThe Dow Chemical Company, Midland, Mich.

The pesticide is one that is effective to kill pests that ingest orcontact the pesticide. Some of the pesticides that can be employed in acomposite material as disclosed herein include, but are not limited tothe following:

1,2 dichloropropane, 1,3 dichloropropene,

abamectin, acephate, acequinocyl, acetamiprid, acethion, acetoprole,acrinathrin, acrylonitrile, alanycarb, aldicarb, aldoxycarb, aldrin,allethrin, allosamidin, allyxycarb, alpha cypermethrin, alpha ecdysone,amidithion, amidoflumet, aminocarb, amiton, amitraz, anabasine, arsenousoxide, athidathion, azadirachtin, azamethiphos, azinphos ethyl, azinphosmethyl, azobenzene, azocyclotin, azothoate,

barium hexafluorosilicate, barthrin, benclothiaz, bendiocarb,benfuracarb, benomyl, benoxafos, bensuliap, benzoximate, benzylbenzoate, beta cyfluthrin, beta cypermethrin, bifenazate, bifenthrin,binapacryl, bioallethrin, bioethanomethrin, biopermethrin, bistrifluron,borax, boric acid, bromfenvinfos, bromo DDT, bromocyclen, bromophos,bromophos ethyl, bromopropylate, bufencarb, buprofezin, butacarb,butathiofos, butocarboxim, butonate, butoxycarboxim,

cadusafos, calcium arsenate, calcium polysulfide, camphechlor,carbanolate, carbaryl, carbofuran, carbon disulfide, carbontetrachloride, carbophenothion, carbosulfan, cartap, chinomethionat,chlorantraniliprole, chlorbenside, chlorbicyclen, chlordane,chlordecone, chlordimeform, chlorethoxyfos, chlorfenapyr, chlorfenethol,chlorfenson, chlorfensulphide, chlorfenvinphos, chlorfluazuron,chlormephos, chlorobenzilate, chloroform, chloromebuform,chloromethiuron, chloropicrin, chloropropylate, chlorphoxim,chlorprazophos, chlorpyrifos, chlorpyrifos methyl, chlorthiophos,chromafenozide, cinerin I, cinerin II, cismethrin, cloethocarb,clofentezine, closantel, clothianidin, copper acetoarsenite, copperarsenate, copper naphthenate, copper oleate, coumaphos, coumithoate,crotamiton, crotoxyphos, cruentaren A &B, crufomate, cryolite,cyanofenphos, cyanophos, cyanthoate, cyclethrin, cycloprothrin,cyenopyrafen, cyflumetofen, cyfluthrin, cyhalothrin, cyhexatin,cypermethrin, cyphenothrin, cyromazine, cythioate,

d-limonene, dazomet, DBCP, DCIP, DDT, decarbofuran, deltamethrin,demephion, demephion O, demephion S, demeton, demeton methyl, demeton O,demeton O methyl, demeton S, demeton S methyl, demeton S methylsulphon,diafenthiuron, dialifos, diamidafos, diazinon, dicapthon,dichlofenthion, dichlofluanid, dichlorvos, dicofol, dicresyl,dicrotophos, dicyclanil, dieldrin, dienochlor, diflovidazin,diflubenzuron, dilor, dimefluthrin, dimefox, dimetan, dimethoate,dimethrin, dimethylvinphos, dimetilan, dinex, dinobuton, dinocap,dinocap 4, dinocap 6, dinocton, dinopenton, dinoprop, dinosam,dinosulfon, dinotefuran, dinoterbon, diofenolan, dioxabenzofos,dioxacarb, dioxathion, diphenyl sulfone, disulfiram, disulfoton,dithicrofos, DNOC, dofenapyn, doramectin,

ecdysterone, emamectin, EMPC, empenthrin, endosulfan, endothion, endrin,EPN, epofenonane, eprinomectin, esfenvalerate, etaphos, ethiofencarb,ethion, ethiprole, ethoate methyl, ethoprophos, ethyl DDD, ethylformate, ethylene dibromide, ethylene dichloride, ethylene oxide,etofenprox, etoxazole, etrimfos, EXD,

famphur, fenamiphos, fenazaflor, fenazaquin, fenbutatin oxide,fenchlorphos, fenethacarb, fenfluthrin, fenitrothion, fenobucarb,fenothiocarb, fenoxacrim, fenoxycarb, fenpirithrin, fenpropathrin,fenpyroximate, fenson, fensulfothion, fenthion, fenthion ethyl,fentrifanil, fenvalerate, fipronil, flonicamid, fluacrypyrim, fluazuron,flubendiamide, flubenzimine, flucofuron, flucycloxuron, flucythrinate,fluenetil, flufenerim, flufenoxuron, flufenprox, flumethrin,fluorbenside, fluvalinate, fonofos, formetanate, formothion,formparanate, fosmethilan, fospirate, fosthiazate, fosthietan,fosthietan, furathiocarb, furethrin, furfural,

gamma cyhalothrin, gamma HCH,

halfenprox, halofenozide, HCH, HEOD, heptachlor, heptenophos,heterophos, hexaflumuron, hexythiazox, HHDN, hydramethylnon, hydrogencyanide, hydroprene, hyquincarb,

imicyafos, imidacloprid, imiprothrin, indoxacarb, iodomethane, IPSP,isamidofos, isazofos, isobenzan, isocarbophos, isodrin, isofenphos,isoprocarb, isoprothiolane, isothioate, isoxathion, ivermectin

jasmolin I, jasmolin II, jodfenphos, juvenile hormone I, juvenilehormone II, juvenile hormone III,

kelevan, kinoprene,

lambda cyhalothrin, lead arsenate, lepimectin, leptophos, lindane,lirimfos, lufenuron, lythidathion,

malathion, malonoben, mazidox, mecarbam, mecarphon, menazon,mephosfolan, mercurous chloride, mesulfen, mesulfenfos, metaflumizone,metam, methacrifos, methamidophos, methidathion, methiocarb,methocrotophos, methomyl, methoprene, methoxychlor, methoxyfenozide,methyl bromide, methyl isothiocyanate, methylchloroform, methylenechloride, metofluthrin, metolcarb, metoxadiazone, mevinphos,mexacarbate, milbemectin, milbemycin oxime, mipafox, mirex, MNAF,monocrotophos, morphothion, moxidectin,

naftalofos, naled, naphthalene, nicotine, nifluridide, nikkomycins,nitenpyram, nithiazine, nitrilacarb, novaluron, noviflumuron,

omethoate, oxamyl, oxydemeton methyl, oxydeprofos, oxydisulfoton,

paradichlorobenzene, parathion, parathion methyl, penfluron,pentachlorophenol, permethrin, phenkapton, phenothrin, phenthoate,phorate, phosalone, phosfolan, phosmet, phosnichlor, phosphamidon,phosphine, phosphocarb, phoxim, phoxim methyl, pirimetaphos, pirimicarb,pirimiphos ethyl, pirimiphos methyl, potassium arsenite, potassiumthiocyanate, pp′ DDT, prallethrin, precocene I, precocene II, precoceneIII, primidophos, proclonol, profenofos, profluthrin, promacyl,promecarb, propaphos, propargite, propetamphos, propoxur, prothidathion,prothiofos, prothoate, protrifenbute, pyraclofos, pyrafluprole,pyrazophos, pyresmethrin, pyrethrin I, pyrethrin II, pyridaben,pyridalyl, pyridaphenthion, pyrifluquinazon, pyrimidifen, pyrimitate,pyriprole, pyriproxyfen,

quassia, quinalphos, quinalphos, quinalphos methyl, quinothion,quantifies,

rafoxanide, resmethrin, rotenone, ryania,

sabadilla, schradan, selamectin, silafluofen, sodium arsenite, sodiumfluoride, sodium hexafluorosilicate, sodium thiocyanate, sophamide,spinetoram, spinosad, spirodiclofen, spiromesifen, spirotetramat,sulcofuron, sulfiram, sulfluramid, sulfotep, sulfur, sulfuryl fluoride,sulprofos,

tau fluvalinate, tazimcarb, TDE, tebufenozide, tebufenpyrad,tebupirimfos, teflubenzuron, tefluthrin, temephos, TEPP, terallethrin,terbufos, tetrachloroethane, tetrachlorvinphos, tetradifon,tetramethrin, tetranactin, tetrasul, theta cypermethrin, thiacloprid,thiamethoxam, thicrofos, thiocarboxime, thiocyclam, thiodicarb,thiofanox, thiometon, thionazin, thioquinox, thiosultap, thuringiensin,tolfenpyrad, tralomethrin, transfluthrin, transpermethrin, triarathene,triazamate, triazophos, trichlorfon, trichlormetaphos 3, trichloronat,trifenofos, triflumuron, trimethacarb, triprene,

vamidothion, vamidothion, vaniliprole, vaniliprole,

XMC, xylylcarb,

zeta cypermethrin and zolaprofos.

Additionally, any combination of the above pesticides can be used.

For more information consult “Compendium of Pesticide Common Names”located at http://www.alanwood.net/pesticides/index.html as of thefiling date of this document. Also consult “The Pesticide Manual” 14thEdition, edited by C D S Tomlin, copyright 2006 by British CropProduction Council.

In one embodiment, the pesticide is one that has an immediate effectupon ingestion by or contact with a pest (referred to herein as an“immediate action” pesticide or a “fast acting” pesticide). For example,insecticides that have immediate killing action upon ingestion bytermites include chlorpyrifos, spinosad, imidacloprid and fipronil, eachof which is well known and available commercially. As used herein, theterm “immediate” is intended to mean that the pesticide typicallyoperates to kill an individual pest before the pest returns to itscolony. In another embodiment, the pesticide is one that exhibits adelayed effect upon ingestion by or contact with a pest (referred toherein as a “delayed action” pesticide). For example, insecticides thathave delayed killing activity upon ingestion by or contact with termitesinclude hexaflumuron and noviflumuron, each of which is well known andavailable commercially. As used herein, the term “delayed” is intendedto mean that the pesticide typically does not operate to kill anindividual pest until after the pest has returned to its colony. Inanother embodiment, the pesticide is selected from the group consistingof lufenuron, diflubenzuron, flufenoxuron and hydramethylnon.

The plastic structural matrix in one embodiment comprises a polymer thathas a melting point of below about 220° C. In another embodiment, theplastic structural matrix comprises a polymer that has a melting pointof below about 200° C. In yet another embodiment, the plastic structuralmatrix comprises a polymer that has a melting point of no greater thanabout 180° C. The plastic structural matrix in another embodimentcomprises a polymer that has a melting point of below about 160° C. Instill yet another embodiment, the plastic structural matrix comprises apolymer that has a melting point of below about 140° C. The processingtemperature used to melt the polymer when making the composite materialis a temperature less than that at which the functionality of thepesticide is nullified. In another embodiment, the thermoplastic polymerincluded in the composite material is one that is palatable to thetarget pest species (also referred to herein as a “pest-ediblepolymer”). In yet another embodiment, the plastic structural matrixcomprises a thermoplastic cellulose derivative. In one preferredembodiment, the matrix includes a cellulose acetate. For example, thecellulose acetate in one embodiment is one with a degree ofpolymerization of from about 50 to about 400 monomer units. In anotherembodiment, the polymer includes cellulose acetate butyrate. Forexample, the cellulose acetate butyrate in one embodiment is one with adegree of polymerization of from about 50 to about 400 units. In anotherembodiment, the cellulose acetate butyrate has a degree ofpolymerization of from about 100 to about 300 units. In yet anotherembodiment, a cellulose acetate butyrate included in the composite hasabout 160 units. In yet another embodiment, the matrix includescellulose acetate propionate. For example, the cellulose acetatepropionate in one embodiment is one with a degree of polymerization offrom about 50 to about 400 units. In another embodiment, the celluloseacetate propionate has a degree of polymerization of from about 100 toabout 300. Alternatively, a wide variety of other polymers can beutilized.

The application also contemplates that the thermoplastic polymer caninclude a single polymer or a mixture of at least two differentpolymers. For example, in one embodiment, the thermoplastic polymerincludes a mixture of a relatively high molecular weight polymer and arelatively low molecular weight polymer. One embodiment, for example,includes a mixture of a cellulose acetate butyrate having from about 50to about 75 monomer units and a cellulose acetate butyrate having fromabout 150 to about 300 monomer units. Another embodiment includes amixture of a cellulose acetate butyrate having about 60 monomer unitsand a cellulose acetate butyrate having about 300 monomer units. Yetanother embodiment includes a mixture of a cellulose acetate butyratehaving about 64 monomer units and a cellulose acetate butyrate havingabout 160 monomer units. In another embodiment, the thermoplasticpolymer includes a mixture of a cellulose acetate propionate having fromabout 50 to about 75 monomer units and a cellulose acetate propionatehaving from about 150 to about 300 monomer units. Another embodimentincludes a mixture of a cellulose acetate propionate having about 60monomer units and a cellulose acetate propionate having about 300monomer units. Yet another embodiment includes a mixture of a celluloseacetate propionate having about 64 monomer units and a cellulose acetatepropionate having about 160 monomer units. The application contemplatesa variety of additional combinations, as would occur to a person ofordinary skill in the art. In addition to mixtures that include polymersof different molecular weights, the application contemplates embodimentsin which the thermoplastic polymer includes a mixture of different typesof polymers. For example, the polymer can include a mixture of two ormore of cellulose acetate, cellulose acetate butyrate and celluloseacetate propionate. Alternatively, the polymer can include a mixture ofone or more of these with one or more other thermoplastic polymers ortwo or more other thermoplastic polymers. The mixture chosen hasphysical properties (i.e., processability features and palatability towood-destroying pests) that are suitable for the uses described herein.

In addition to the polymer, the food material and the pesticide, otheringredients can optionally be included in the composite material. Forexample, some ingredients can be included to increase the stability orshelf life of the pesticide included in the composite. Other ingredientscan be selected to improve the processability of the mixture, or toprovide an advantageous effect after the composite material is formed.Still other ingredients can be selected, for example, to attract peststo the baits or to stimulate feeding. The composite materials disclosedherein can also include or be used with herbicides and fungicides, bothfor reasons of economy and synergy. The composite materials disclosedherein can also include or be used with antimicrobials, bactericides,defoliants, safeners, synergists, algaecides, attractants, desiccants,pheromones, repellants, animal dips, avicides, disinfectants,semiochemicals, and molluscicides (these categories not necessarilymutually exclusive) for reasons of economy, and synergy.

The composite material can be fabricated by way of a process thatutilizes a combination of compounding and extrusions or molding to formarticles composed of the composite material. The present application isnot intended to be limited to the manufacture of articles having aspecific shape, or “macrostructure.” Rather, a wide variety of shapesare envisioned. Articles made in accordance with the application can beformed into a wide variety of shapes by extrusion, by post-extrusionprocessing, by original mold design, by post-molding processing or by acombination thereof.

To make a composite material in accordance with one embodiment, amixture of a granular or particulate thermoplastic polymer, a pesticideand a cellulosic material is provided and the mixture is then compoundedto mix the components, and extruded or molded at a predeterminedtemperature and pressure. The polymer, the cellulosic material and thepesticide can be combined using standard mixing or compoundingtechniques to mix the components and drive off excess moisture. Forexample, the materials can be mixed in a rotational mixer or compoundingextruder. Heat is applied if needed to bring the mixture to atemperature at least as high has the melting point or glass transitiontemperature of the polymer (i.e., a temperature suitable to soften theamorphous portion of the polymer) but not to a temperature at which thefunctionality of the pesticide is nullified. The thermoplastic polymersoftens upon reaching its melting point or glass transition temperature,making it pliable or plastic and therefore suitable for shaping, such asby extrusion. Preferably, the temperature is at least as high as themelting point of the polymer, but not so high that pesticidefunctionality is nullified. In one embodiment, the processingtemperature is no greater than about 220° C., such as, for example, fromabout 90° C. to about 220° C. In another embodiment, the processingtemperature is from about 170° C. to about 220° C. In anotherembodiment, the processing temperature is no greater than about 200° C.,such as, for example, from about 90° C. to about 200° C. In anotherembodiment, the processing temperature is from about 150° C. to about200° C. In another embodiment, the processing temperature is no greaterthan about 180° C., such as, for example, from about 90° C. to about180° C. In another embodiment, the processing temperature is from about130° C. to about 180° C. In another embodiment, the processingtemperature is no greater than about 160° C., such as, for example, fromabout 90° C. to about 160° C. In another embodiment, the processingtemperature is from about 110° C. to about 160° C. In anotherembodiment, the processing temperature is no greater than about 140° C.,such as, for example, from about 90° C. to about 140° C. In anotherembodiment, the processing temperature is from about 100° C. to about140° C. One skilled in the art will recognize that higher temperaturesmay be needed, and that the processing temperature may be optimized toallow the polymer to be processed as long as the temperature is notraised to a point that results in substantial harm to other componentsof the composite, such as, for example, charring the cellulosic foodmaterial or nullifying the functionality of the pesticide. A person ofordinary skill in the art will also understand that the inclusion of asolvent in the mixture can modify the softening temperature of thethermoplastic polymer material. In embodiments in which a solvent ispresent, it is understood that softening at the surface of a polymer, asmodified by the solvent, might begin at a temperature that is lower thanthe natural melting point of the polymer in the absence of the solvent.In other words, temperatures below the natural melting point of thepolymer may be suitable molding temperatures in embodiments in which thesolvent is effective to soften the surface of the polymer at atemperature below its natural melting point.

A wide variety of extrusion or molding techniques can be used, manyexamples of which are known in the art. While it is not intended thatthe present application be limited by any theory, it is believed that,under extrusion or molding conditions applied in methods describedherein, the polymer granules become softened, tacky or fully melted.When this occurs, pressure exerted upon the mixture causes softenedpolymer granules to contact one another and adhere together or causesthe polymer to fully melt, whereby the molten polymer forms a continuousphase in the mixture. The temperature at which the compression isapplied is a temperature less than that which would damage or denaturethe pesticide but high enough to achieve a desired level of polymerparticle adhesion or polymer melting. It is understood that a widevariety of material specifications (such as polymer type, polymer size,granule size distribution and ratio of ingredients) and also a widevariety of process parameters (such as temperature and pressure) can beused to provide articles having various advantageous characteristics. Itis within the ability of a skilled artisan, armed with the descriptionof the present application, to select, without undue experimentation,advantageous combinations of materials and parameters to providearticles having differing levels of pesticide, different degrees ofpalatability to various wood-destroying pests, and different physicalproperties.

As will be appreciated by a person skilled in the art upon considerationof the descriptions herein, one aspect of the present application is amethod for making a composite material that includes: (1) providing amixture of a softened or molten thermoplastic polymer having a softeningor melting point below about 220° C., a cellulosic food material that ispalatable to at least one species of wood-destroying pest and apesticide that is toxic to the pest; (2) forming the mixture to providea workpiece having a desired shape; and (3) cooling the workpiece to atemperature below the softening or melting point of the plastic toprovide a solid composite article. The heated mixture can optionallyalso include a plasticizer. In one embodiment, the quantity ofplasticizer is at least about 1% by weight relative to the total weightof the mixture. In another embodiment, the quantity of plasticizer is atleast about 1.5% by weight relative to the total weight of the mixture.In yet another embodiment, the quantity of plasticizer is from about 1%to about 5% by weight relative to the total weight of the mixture. Instill another embodiment, the quantity of plasticizer is at least about4.2% by weight relative to the total weight of the mixture. In oneidentified formulation, the polymer in the mixture is a celluloseacetate polymer and the plasticizer is a plasticizer for celluloseacetate. For example and without limitation, the plasticizer can be anester of polyol and/or an ester of a hydroxyl carboxylic acid. Examplesof suitable plasticizers include glycerol triacetate, triethylene glycoldiacetate, an ester of citric acid and an ester of phthalic acid. Othersuitable plasticizers include mixtures of adipate plasticizers such as,for example, diisobutyl adipate and dioctyl adipate at similar totalconcentrations of 1% to 5% of the extrusion matrix. In one embodiment,the diisobutyl adipate and dioctyl adipate are present in the mixture ina ratio of about 3:1 wt/wt.

In one manner of practicing the method, the molten mixture is providedby mixing the polymer, the food material and the pesticide to form amixture and then compounding said mixture under elevated pressure andtemperature to form a molten material. In another manner of practicingthe method, the method includes forming pellets or flakes of the mixtureprior to compounding. In one manner of making the composite materialarticles, all of the components are mixed together and then the mixtureis heated above the melting point of the thermoplastic polymer includedtherein, e.g. up to about 220° C. in some embodiments, in a device, suchas a twin screw mixer, that is capable of additional mixing followed byextrusion through a die, which imparts a specific cross-sectionalprofile to the composite material, and then cooling in a water bath orspray. In another manner of forming articles composed of the compositematerial, the polymers, cellulosic food materials and pesticides arecombined within an extruder under positive pressure and at elevatedtemperature and are thereafter extruded to provide an elongatedworkpiece. Thereafter, cooling water is applied to the workpiece. Thecooling can be achieved, for example, by applying a water bath to theworkpiece or by spraying the workpiece with water.

The thermoplastic polymer levels in the mixture in one embodiment arefrom about 5% to about 50% of the total composite weight, with theremainder of the mixture comprising a cellulosic material (about 50% toabout 85%), a pesticide (from about 0.001% to about 5%) and, optionally,lubricants (e.g., up to about 5%) and/or other processing additiveswhich are used to help improve the processability of the mixture or theproperties of the product. In another embodiment, the mixture includesfrom about 10% to about 40% polymer, from about 60% to about 85%cellulosic material and from about 0.001% to about 5% pesticide. In yetanother embodiment, the mixture includes from about 15% to about 30%polymer, from about 70% to about 85% cellulosic material and from about0.001% to about 5% pesticide. In other embodiments, the pesticide ispresent in an amount in the range of from about 0.4% to about 5%.

In another manner of practicing the method, the food material, such as,for example, purified alpha cellulose, is first pre-loaded with thepesticide (also referred to herein as “active ingredient” or “AI”). Inone manner of pre-loading, the pesticide is sprayed directly oncellulose particles, and the mixture of cellulose particles andpesticide is then compacted and broken into prills, which include thecellulose food material and the pesticide therein. When this approach isused, the pesticide is referred to as “incorporated in cellulose,” andthis method is referred to as an “incorporated in cellulose” method. Inanother manner of pre-loading the food material with an AI, pre-formedprills of cellulose (which are available commercially, and can beobtained from International Fibers) are sprayed with the pesticide toprovide a pre-loaded cellulose material. When this approach is used, thepesticide is referred to as “sprayed on cellulose,” and this method isreferred to as a “sprayed on cellulose” method. The cellulose/pesticideprills (or optionally the uncompacted cellulose/pesticide mixture) ismixed with the thermoplastic polymer material, and this mixture is thenextruded at a temperature above the melting point of the thermoplasticpolymer material. In one embodiment, the thermoplastic polymer materialincludes cellulose acetate butyrate. For example, the cellulose acetatebutyrate can include a mixture of a cellulose acetate butyrate having amolecular weight of about 16,000 and a cellulose acetate butyrate havinga molecular weight of about 40,000. When this mixture is used, it can beextruded at a temperature of 140° C. to 150° C. A lubricant can also beincluded to aide the flow of the matrix through an extrusion die. In oneembodiment, the lubricant is calcium stearate.

In another manner of practicing the method cellulose prills are firstcompounded (for example, in a Gelimat compounder) with the thermoplasticpolymer to provide cellulose/plastic prills, and then the pesticide isspray applied to the post-compounded cellulose/plastic prills. Calciumstearate can optionally be mixed with the post-compounded batch prior tospraying the pesticide onto the material. After the pesticide isapplied, the mixture is extruded or otherwise molded. In experimentalwork using cellulose acetate butyrate (CAB), discussed further in theExamples below, a Gelimat compounder is used to blend and partially meltthe CAB with other solid components through the use of intense shear andthe generation of heat. In the Gelimat compounder, a 1000 HP motordrives a mixing paddle in a chamber having about a 1-cubic-foot volume,which contains the solids to be compounded. This mixing step distributesthe CAB and also drives off water, which is deleterious in the extrusionprocess.

In another manner of practicing the method, the method includes: (a)adding the food material and the pesticide to an extruder mixingcontainer; (b) contacting a hot thermoplastic polymer with the foodmaterial and pesticide to produce a foodmaterial/pesticide/thermoplastic polymer mixture; and (c) contacting thefood material/pesticide/thermoplastic polymer mixture with a die toprovide shape to the food material/pesticide/thermoplastic polymermixture and to produce the workpiece. In one embodiment, the foodmaterial includes wood fibers.

In an alternate embodiment, a mixture of particulate polymer, cellulosicfood material and pesticide, and optionally other ingredients, is formedinto a composite material by injection molding. Alternatively or inaddition, the mixture can be combined and pressed in a Carver press orother compression molding device. The composite material when injectioninto a mold cavity at a positive pressure and an elevated temperaturetakes the form of the mold and upon cooling produces a compositematerial as described above.

A composite material as provided herein can be used as a monitor or baitfor a pest control device. In one example, the composite material can beused as a stand-alone bait for attracting and terminating pests as asingle-step pesticide delivery tool without the need for monitoring bypest control professionals to determine whether such pests are presentin a given area. Alternatively, it can be used with monitoring steps fordetermining the presence or absence of wood destroying pests. Forexample, it can be used as a replacement monitor or a bait in an alreadyexisting termite bait station such as, for example, the SENTRICON®Termite Colony Elimination bait station, as described further below withreference to FIGS. 1-7.

FIG. 1 illustrates pest control system 20. System 20 is arranged toprotect building 22 from damage due to pests, such as subterraneantermites. System 20 includes a number of pest control devices 110positioned about building 22. In FIG. 1, only a few of devices 110 arespecifically designated by reference numerals to preserve clarity.System 20 also includes interrogator 30 to gather information aboutdevices 110. Data gathered from devices 110 with interrogator 30 iscollected in Data Collection Unit (DCU) 40 through communicationinterface 41.

Referring additionally to FIG. 2, certain aspects of the operation ofsystem 20 are illustrated. In FIG. 2, a pest control service provider Pis shown operating interrogator 30 to interrogate pest control devices110 located at least partially below ground G using a wirelesscommunication technique. In this example, interrogator 30 is shown in ahand-held form convenient for sweeping over ground G to establishwireless communication with installed devices 110. In an alternativeexample, interrogator 30 may include contacts that are configured totemporarily engage pest control devices 110 to electrically coupletherewith in order to interrogate pest control devices 110. Additionalaspects of system 20 and its operation are described below, but firstfurther details concerning a representative pest control device 110 aredescribed with reference to FIGS. 3-7.

FIGS. 3-7 illustrate various features of pest control device 110. Toinitially detect pests, pest control device 110 is internally configuredwith pest monitoring assembly 112. Referring more specifically to FIGS.3 and 4, pest monitoring assembly 112 is illustrated along centerlineassembly axis A. Axis A coincides with the view planes of both FIGS. 3and 4; where the view plane of FIG. 4 is perpendicular to the view planeof FIG. 3.

Pest monitoring assembly 112 includes sensor subassembly 114 belowcommunication circuit subassembly 116 along axis A. Sensor subassembly114 includes two (2) bait members 132 (see FIGS. 3 and 6). Bait members132 are each made from a bait material for one or more selected speciesof pests. For example, bait members 132 can each be made of a materialthat is a favorite food of such pests. In one example directed tosubterranean termites, bait members 132 can each be in the form of asoft wood block without a pesticide component. In other examples fortermites, one or more of bait members 132 can include a pesticide, havea composition other than wood, or have a combination of these features.In still other examples where pest control device 110 is directed to atype of pest other than termites, a correspondingly differentcomposition of each bait member 132 is typically used. One or both ofbait members 132 can comprise a pesticidal composite material asdescribed hereinabove when it is desired to use a bait member thatincludes a pesticide.

Sensor subassembly 114 also includes sensor 150. Sensor 150 is depictedbetween bait members 132 in FIGS. 3 and 6; where FIG. 6 is a more fullyassembled view of pest control device 110 than FIG. 3. Sensor 150 isgenerally elongated and has end portion 152 a opposite end portion 152 bas shown in FIGS. 4 and 6. A middle portion of sensor 150 is representedby a pair of adjacent break lines separating portions 152 a and 152 b inFIG. 4, and bait members 132 are not shown in FIG. 4 to preventobscuring the view of sensor 150.

Sensor 150 includes substrate 151. Substrate 151 carries conductor 153that is arranged to provide sensing element 153 a in the form of anelectrically conductive loop or pathway 154 shown in the broken view ofFIG. 4. Along the middle sensor portion represented by the break linesof FIG. 4, the four segments of pathway 154 continue along a generallystraight, parallel route (not shown), and correspondingly join the fourpathway segments of end portion 152 a ending at one of the break lineswith the four pathway segments of end portion 152 b ending at another ofthe break lines. Pathway 154 terminates with a pair of electricalcontact pads 156 adjacent substrate edge 155 of end portion 152 a.

Substrate 151 and/or conductor 153 are/is comprised of one or morematerials susceptible to consumption or displacement by the pests beingmonitored with pest monitoring assembly 112. These materials can be afood substance, a nonfood substance, or a combination of both for theone or more pest species of interest. Indeed, it has been found thatmaterials composed of nonfood substances will be readily displacedduring the consumption of adjacent edible materials, such as baitmembers 132. In certain embodiments, one or more of substrate 151 orconductor 153 can be composed of a pesticidal composite material asdescribed hereinabove. As substrate 151 or conductor 153 are consumed ordisplaced, pathway 154 is eventually altered. This alteration can beutilized to indicate the presence of pests by monitoring one or morecorresponding electrical properties of pathway 154 as will be more fullydescribed hereinafter. Alternatively, substrate 151 and/or conductor 153can be oriented with respect to bait members 132 so that a certaindegree of consumption or displacement of bait members 132 exerts amechanical force sufficient to alter the electrical conductivity ofpathway 154 in a detectable manner. For this alternative, substrate 151and/or conductor 153 need not be directly consumed or displaced by thepest of interest.

Pest monitoring assembly 112 further includes circuit subassembly 116coupled to sensor subassembly 114. Circuit subassembly 116 is arrangedto detect and communicate pest activity as indicated by a change in oneor more electrical properties of pathway 154 of sensor subassembly 114.Circuit subassembly 116 includes circuit enclosure 118 for housingcommunication circuitry 160 and a pair of connection members 140 fordetachably coupling communication circuitry 160 to sensor 150 of sensorsubassembly 114. Enclosure 118 includes cover piece 120, o-ring 124, andbase 130, that each have a generally circular outer perimeter about axisA. Enclosure 118 is shown more fully assembled in FIG. 4 relative toFIG. 3. Cover piece 120 defines cavity 122 bounded by inner lip 123.Base 130 defines channel 131 (shown in phantom) sized to receive o-ring124 and also includes outer flange 133 configured to engage inner lip123 when base 130 is assembled with cover piece 120 (see FIG. 4).

Communication circuitry 160 is positioned between cover piece 120 andbase 130. Communication circuitry 160 includes coil antenna 162 andprinted wiring board 164 carrying circuit components 166. Referring alsoto FIG. 5, a top view is shown of an assembly of base 130, connectionmembers 140, and wireless communication circuitry 160. In FIG. 5, axis Ais perpendicular to the view plane and is represented by like labeledcross-hairs. Base 130 includes posts 132 to engage mounting holesthrough printed wiring board 164. Base 130 also includes mounts 134 toengage coil antenna 162 and maintain it in fixed relation to base 130and printed wiring board 164 when assembled together. Base 130 furtherincludes four supports 136 each defining opening 137 therethrough asbest illustrated in FIG. 4. Base 130 is shaped with a centrally locatedprojection 138 between adjacent pairs of supports 136. Projection 138defines recess 139 (shown in phantom in FIG. 3).

Referring generally to FIGS. 3-5, connection members 140 each include apair of connection nubs 146. Each nub 146 has neck portion 147 and headportion 145 that extend from opposing end portions of the respectiveconnection member 140. For each connection member 140, projection 148 ispositioned between the corresponding pair of nubs 146. Projection 148defines recess 149. Connection members 140 are formed from anelectrically conductive, elastomeric material. In one embodiment, eachconnection member 140 is made from a carbon-containing silicone rubber,such as compound 862 available from TECKNIT, having a business addressof 129 Dermody Street, Cranford, N.J. 07016. Nonetheless, in otherembodiments, a different composition can be used.

To assemble each connection member 140 to base 130, the correspondingpair of nubs 146 is inserted through a respective pair of openings 137of supports 136, with projection 148 extending into recess 139. Headportion 145 of each of nubs 146 is sized to be slightly larger than therespective opening 137 through which it is to pass. As a result, duringinsertion, head portions 145 are elastically deformed until fullypassing through the respective opening 137. Once head portion 145extends through opening 137, it returns to its original shape with neck147 securely engaging the opening margin. By appropriate sizing andshaping of head portion 145 and neck portion 147 of nubs 146, openings137 can be sealed to resist the passage of moisture and debris when base130 and connection members 140 are assembled together. As shown in FIG.5, printed wiring board 164 contacts one nub 146 of each connectionmember 140 after assembly.

After connection members 140 are assembled with base 130, enclosure 118is assembled by inserting base 130 into cavity 122 with o-ring 124carried in channel 131. During insertion, cover piece 120 and/or base130 elastically deform so that flange 133 extends into cavity 122 beyondinner lip 123, such that cover piece 120 and base 130 engage each otherwith a “snap-fit” type of connection. The angled profile of the outersurface of base 130 facilitates this form of assembly. Once cover piece120 and base 130 are connected in this manner, o-ring 124 provides aresilient seal to resist the intrusion of moisture and debris intocavity 122. The inner surface of cover piece 120 engaged by base 130 hasa complimentary profile that can also assist with sealing.

After communication circuit subassembly 116 is assembled, sensor 150 isassembled to subassembly 116 by asserting end portion 152 a into recess149 of each connection member 140 carried by base 130. Connectionmembers 140 are sized to be slightly elastically deformed by theinsertion of end portion 152 a into recess 149, such that a biasingforce is applied by connection members 140 to end portion 152 a tosecurely hold sensor 150 in contact therewith. Once end portion 152 a isinserted into connection members 140, each pad 156 is electricallycontacted by a different one of connection members 140. In turn, eachnub 146 that contacts printed wiring board 164 electrically couplespathway 154 to printed wiring board 164.

Referring to FIG. 6, an exploded view of pest control device 110 andpest monitoring assembly 112 is depicted. In FIG. 6, sensor subassembly114 and circuit subassembly 116 are shown assembled together and nestedin carrying member 190 to maintain pest monitoring assembly 112 as aunit. Carrying member 190 is in the form of a frame that includes base192 attached to opposing side members 194. Only one of side members 194is fully visible in FIG. 6, with the other extending from base 192 alongthe hidden side of pest monitoring assembly 112 in a like manner. Sidemembers 194 are joined together by bridge 196 opposite base 192. Bridge196 is arranged to define a space 198 contoured to receive the assembledenclosure 118 of circuit subassembly 116.

Pest control device 110 includes housing 170 with removable cap 180arranged for placement in the ground as shown, for example, in FIG. 2.Housing 170 defines chamber 172 intersecting opening 178. Pestmonitoring assembly 112 and carrying member 190 are sized for insertioninto chamber 172 through opening 178. Housing 170 has end portion 171 aopposite end portion 171 b. End portion 171 b includes tapered end 175to assist with placement of pest control device 110 in the ground asillustrated in FIG. 2. End 175 terminates in an aperture (not shown). Incommunication with chamber 172 are a number of slots 114 defined byhousing 170. Slots 174 are particularly well-suited for the ingress andegress of termites from chamber 172. Housing 170 has a number ofprotruding flanges a few of which are designated by reference numerals176 a, 176 b, 176 c, 176 d, and 176 e in FIG. 6 to assist withpositioning of pest control device 110 in the ground.

Once inside chamber 172, pest monitoring assembly 112 can be secured inhousing 170 with cap 180. Cap 180 includes downward prongs 184 arrangedto engage channels 179 of housing 170. After cap 180 is fully seated onhousing 170, it can be rotated to engage prongs 184 in a latchingposition that resists disassembly. This latching mechanism can include apawl and detent configuration. Slot 182 can be used to engage cap 180with a tool, such as a flat-bladed screwdriver, to assist in rotatingcap 180. It is preferred that carrying member 190, base 130, cover piece120, housing 170, and cap 180 be made of a material resistant todeterioration by expected environmental exposure and resistant toalteration by the pests likely to be detected with pest control device110. In one form, these components are made from a polymeric resin likepolypropylene or CYCOLAC AR polymeric plastic material available fromGeneral Electric Plastics, having a business address of One PlasticsAvenue, Pittsfield, Mass. 01201.

Typically, pest monitoring assembly 112 is placed in chamber 172 afterhousing 170 is at least partially installed in the ground in the regionto be monitored. Assembly 112 is configured to detect and report pestactivity. In one mode of operation, pest control device 110 isreconfigured to deliver a pesticide after pest activity is detected withpest monitoring assembly 112. FIG. 7 is an exploded assembly view of oneexample of such a reconfiguration. In FIG. 7, pest control device 110utilizes pesticide delivery assembly 119 as a substitute for pestmonitoring assembly 112 after pest activity has been detected.Substitution begins by rotating cap 180 in a direction opposite thatrequired to latch it, and removing cap 180 from housing 170. Typically,the removal of cap 180 is performed with housing 170 remaining at leastpartially installed in the ground. Pest monitoring assembly 112 is thenextracted from housing 170 by pulling carrying member 190. It has beenfound that application of pest control device 110 to pests such astermites can lead to the accumulation of a substantial amount of dirtand debris in chamber 172 before pest monitoring assembly 112 isremoved. This accumulation can hamper the removal of pest monitoringassembly 112 from chamber 172. As a result, member 190 is preferablyarranged to withstand at least 40 pounds (lbs.) of pulling force, andmore preferably at least 80 lbs. of pulling force.

After pest monitoring assembly 112 is removed from chamber 172,pesticide delivery assembly 119 is placed in chamber 172 of housing 170through opening 178. Pesticide delivery assembly 119 includes pesticidebait tube 1170 defining chamber 1172. Chamber 1172 contains pesticidebearing matrix member 1173, which can be composed of the pesticidalcomposite material described hereinabove. Tube 1170 has a threaded end1174 arranged for engagement by cap 1176, which has complimentary innerthreading (not shown). Cap 1176 defines aperture 1178. Circuitsubassembly 116 is detached from sensor 150 before, during, or afterremoval of pest monitoring assembly 112 from housing 170. Aperture 1178is accordingly sized and shaped to securely receive circuit subassembly116 after disassembly from pest monitoring assembly 112. After pesticidedelivery assembly 119 is configured with circuit subassembly 116, it isplaced in chamber 172, and cap 180 can re-engage housing 170 in themanner previously described.

In view of the above, a person skilled in the art will appreciate thatthe present application in one aspect provides a pest control devicethat includes a pesticidal bait operable to be consumed or displaced byone or more species of pest; and a housing at least partially enclosingsaid bait. The pesticidal bait comprises a composite material includinga plastic structural matrix, a cellulosic food material contained withinthe matrix that is palatable to the pest and a pesticide containedwithin the matrix that is toxic to the pest. The device can also includea pest sensing circuit or be configured to alternatingly include a pestsensing circuit and a pesticidal bait. In another aspect, theapplication provides a pest control system that includes at least twopest control devices each arranged to be spaced apart from one anotherin an area to be protected from one or more pests. At least one of thepest control devices includes, or is configured to alternatinglyinclude, a bait that is operable to be consumed or displaced by the pestand that includes a composite material including a plastic structuralmatrix, a cellulosic food material contained within the matrix that ispalatable to the pest and a pesticide contained within the matrix thatis toxic to the pest.

In another aspect, the application provides a method that includes: (1)providing a pest control device including a pesticidal bait for one ormore species of pest, the bait including a composite material includinga plastic structural matrix, a cellulosic food material contained withinthe matrix that is palatable to the pest and a pesticide containedwithin the matrix that is toxic to the pest; and (2) installing thedevice in an area to be protected from the pests. In one manner ofpracticing the method, the device is one that further includes a pestsensor and communication circuitry coupled to the pest sensor. In oneexample, the sensor includes a pest sensing circuit, and the pestsensing circuit includes an electrically conductive loop arranged to bealtered during consumption or displacement of the bait for the pestcontrol devices. The loop is coupled to the communication circuitry toprovide a two-state signal, a first state of the signal corresponding toan electrically open condition of the loop, and a second state of thesignal corresponding to an electrically closed condition of the loop.

In another aspect of the present application, a composite materialdescribed herein can be used as a wood substitute material forstructural applications that typically call for the use of lumber. Thewood substitute material includes a composite material comprising aplastic structural matrix, a cellulosic food material contained withinthe matrix that is palatable to the pest and a pesticide containedwithin the matrix that is toxic to the pest. A composite material asdescribed herein can be used as a wood substitute for structuralcomponents, such as, for example, structural parts for windows anddoors, moldings, or fascia. When the wood substitute material isconsumed or displaced by a wood-destroying pest, the pesticide thereinwill operate to kill some or all of the wood-destroying pests, therebypreventing further damage to the wood substitute material.

The subject matter of the present application will be further describedwith reference to the following specific Examples. It will be understoodthat these Examples are intended to be illustrative and not restrictivein nature.

EXAMPLES Example One Production of Extruded Composite Materials (Run 1)

Purified cellulose was obtained from International Fiber as severalfiber lengths and bulk densities. The fibers tested included AlphaCelBH100, AlphaCel BH200, briquetted BH100, SolkaFloc special granular andSolkaFloc fine granular. For some runs, the AlphaCel BH100 wasbriquetted to form material of higher bulk density. SolkaFloc finegranular and special granular cellulose were found to be suitablestarting materials for mixture with the thermoplastic to form acompounded extruder feed stock.

Table 1 below shows the fibers that were tested in the studies describedherein. The studies have all produced products that have been wellaccepted by termites as measured by mass of the extruded materialconsumed when compared with MD-499, the aspen wood blocks currently usedin SENTRICON® Termite Stations. Different lengths and physical forms ofpurified cellulose fiber were tested in attempts to identify the bestfiber and fiber form for use in the extrusion process.

TABLE 1 Fibers Tested in Extrusion Process Cellulose Length Fiber FiberED (μm) Form Comments AlphaCel 40 Powder Fiber low bulk density - doesnot BH-100 process well, bridges in feeders AlphaCel 35 Powder Fiber lowbulk density does not BH-200 process well, bridges in feeders AlphaCel150 Flakes Fiber density higher, processed well, C-40 some areas ofuntreated fiber (chunks of fiber) AlphaCel 400 Flakes Fiber densityhigher, processed well, C-10 some areas of untreated fiber (chunks offiber) SolkaFloc 75 Granules Fine granules process well, bulk Specialdensity higher so flows well without Granular bridging in feedersBriquetted- 40 Briquettes Fiber very dense. Gelimat broke AlphaCelbriquettes to mix with thermoplastic. BH-100 Incomplete break-upobserved in final product.

Reported physical characteristics for the AlphaCell BH-100 materialinclude an average fiber length of 40 microns, water permeability of 3darcies cc/g (determined using a 20 gram sample at 5 psi), a wet bulkdensity of 18 pounds per cubic foot and screen analysis of 0% on 40Mesh, not less than 90% through 100 Mesh and not less than 70% through200 Mesh.

Reported physical characteristics for the AlphaCell BH-200 materialinclude an average fiber length of 35 microns, bulk volume 2.1-2.6 cc/g,water retention of 3.0% g/g and screen analysis of 0% on 40 Mesh,93-100% through 100 Mesh and 75-100% through 200 Mesh.

Reported physical characteristics for the AlphaCell C-40 materialinclude an average fiber length of 120 microns, water permeability of 18darcies cc/g (determined using a 20 gram sample at 5 psi), a wet bulkdensity of 9 pounds per cubic foot and screen analysis of less than 1%on 40 Mesh, not more than 95% through 100 Mesh and not more than 50%through 200 Mesh.

Reported physical characteristics for the AlphaCell C-10 materialinclude an average fiber length of 290 microns, water permeability of 28darcies cc/g (determined using a 20 gram sample at 5 psi), a wet bulkdensity of 6.5 pounds per cubic foot and screen analysis of less than15% on 40 Mesh, less than 60% through 100 Mesh and less than 25% through200 Mesh.

Reported physical characteristics for the SolkaFloc Special Granularmaterial include a bulk volume of 28.0 pounds per cubic foot, waterretention of 3.5 g/g and screen analysis of not less than 80% on 40 Meshand not less than 2% through 200 Mesh.

Briquetted AlphaCel BH-100 was made by adding water to AlphaCel BH-100and forming the material into briquettes using a Komarek compactor.Active version of this material would have hexaflumuron or noviflumuronsprayed onto the powder prior to briquetting.

Several different types of thermoplastic polymers were used in thesetrials. Examples include Cellulose Acetate Propionate (CAP), CelluloseAcetate Butyrate (CAB) and Polylactic Acid (PLA). These plastics whenmixed with cellulose were eaten by the termites. Initial trials wereconducted with CAP, which was processed at a temperature of about 180 to200° C. This temperature is quite high relative to the melting points ofHexaflumuron and Noviflumuron. Processing the matrix at this hightemperature in a Gelimat made the product susceptible to charring orpossible ignition if mixed at high shear for too long. The high shearincreases temperature quickly and at temperatures above about 220° C.,the cellulose would char. PLA was processed at approximately 220° C. Atthis temperature, the cellulose is quite susceptible to charring soattention was turned to CAB.

The polymer CAB (processing temperature 130-140° C.) was selected toreduce the processing temperature of the extrusions, which has multiplebenefits. For example, the fiber/thermoplastic matrix is not assusceptible to charring or burning at the lower temperature whenprocessing through the compounding and extrusion step. In addition,processing at these lower temperatures prevents the degradation oftemperature sensitive pesticides.

The form and physical state of the thermoplastic polymers wereinvestigated. Pelletized thermoplastic containing plasticizers was usedinitially. This material worked satisfactorily after the plasticizercontent was optimized to produce the best termite feeding of theextruded matrix. Thermoplastic that is available in a powder form wasfound to mix better with the cellulose fiber and was found easier tocompound. Both the CAP and CAB were used as powdered plastics. Differentmolecular weights of the plastics were mixed to optimize flow of thethermoplastic in the fiber matrix. The mixture of polymers was selectedto produce two effects. The high molecular weight polymer was selectedto produce structural strength to the profile and the low molecularweight polymer was selected to provide improved flow for wetting andviscosity reduction of the polymer/cellulose melt. The CAB polymersselected were CAB-531-1 (high molecular weight polymer) mixed withCAB-551-0.01 (low molecular weight polymer).

Cellulose Acetate Butyrate CAB-531-1 is a cellulose ester commerciallyavailable from Eastman. CAB-531-1 is soluble in a wide range ofsolvents, and is a relatively flexible resin, requiring lowerplasticizer modification than other, less flexible resins. Reportedproperties of CAB-531-1 include the following:

Property Typical Value, Units Butyryl Content 50 wt % Acetyl Content 2.8wt % Hydroxyl Content  1.7% Viscosity^(a) 5.6 poise Color^(b) 50 ppmHaze^(b) 15 ppm Acidity as Acetic Acid 0.02 wt % Ash Content 0.05%Refractive Index 1.475 Heat Test @ 160° C. for 8 hr Tan melt MeltingPoint 135-150° C. Glass Transition Temperature (Tg) 115° C. SpecificGravity 1.17  Wt/Vol (Cast Film) 1.17 kg/L (9.75 lb/gal) Bulk DensityPoured 480 kg/m3 (30 lb/ft3) Tapped 576 kg/m3 (36 lb/ft3) DielectricStrength 787-984 kv/cm (2-2.5 kv/mil) Molecular Weight^(c) M_(n)40000      Tukon Hardness 15 Knoops ^(a)Viscosity determined by ASTMMethod D 1343. Results converted topoises (ASTM Method D 1343) using thesolution density for Formula A as stated in ASTM Method D 817 (20%Cellulose ester, 72% acetone, 8% ethyl alcohol). ^(b)Determination ofcolor and haze made on CAB solutions using Pt—Co standard (color) and amonodisperse latex suspension (haze). Analysis performed with a GardnerModel XL-835 colorimeter. ^(c)Polystyrene equivalent number averagemolecular weight determined by gel permeation chromatography.

Cellulose Acetate Butyrate CAB-551-0.01 is a cellulose estercommercially available from Eastman with high butyryl content and lowASTM(A) viscosity, which significantly affects it solubility andcompatibility. CAB-551-0.01 is soluble in styrene and methylmethacrylate monomers and will tolerate more aliphatic and aromatichydrocarbon diluent than higher viscosity materials. The solubility ofCAB-551-0.01 in alcohol/aromatic hydrocarbon mixtures permits the choiceof a wide range of solvents and solvent combinations. CAB-551-0.01 is adry, white free-flowing powder convenient to handle. Reported propertiesof CAB-551-0.01 include the following:

Property Typical Value, Units Butyryl Content 53 wt % Acetyl Content 2wt % Hydroxyl Content 1.5% Viscosity^(a) 0.038 poise Color 100 ppm Haze25 ppm Acidity as Acetic Acid 0.02 wt % Melting Point 127-142° C. GlassTransition Temperature (Tg) 85° C. Char Point 260° C. Wt/Vol (Cast Film)1.16 kg/L (9.67 lb/gal) Molecular Weight^(b) M_(n) 16000 Tukon Hardness15 Knoops ^(a)Viscosity determined by ASTM Method D 1343. Resultsconverted to poises (ASTM Method D 1343) using the solution density forFormula A as stated in ASTM Method D 817 (20% Cellulose ester, 72%acetone, 8% ethyl alcohol). ^(b)Polystyrene equivalent number averagemolecular weight determined by gel permeation chromatography.

Calcium stearate was used as a lubricant in the extrusions. Thismaterial mixes well with the fiber/thermoplastic matrix and assists flowthrough the extrusion die. The calcium stearate has a meltingtemperature close to that of the extrusion matrix and lubricates theflow of matrix through the die quite well. Additional lubricants, suchas, for example, other metal stearates and other waxes or commerciallubricants are believed to suitable alternatives to calcium stearate forextrusion and will be investigated in subsequent experiments. Lubricantsthat do not interfere significantly with termite feeding are preferred.

Processing the fiber of the extrusions included applying the pesticideto the fiber using a ribbon blender. A 50% concentrate of eitherHexaflumuron or Noviflumuron was sprayed on the fiber to assure evenmixing of the pesticide with the fiber. Concentrations were adjusted toaccount for the concentration of fiber relative to the total matrixcomposition to deliver approximately 0.5% pesticide in the extrudedcomposite material. An estimated additional amount of pesticide wasincluded to account for loss of pesticide in processing. Processing wasalso accomplished using air milled technical mixed with calcium stearateand then this mixture added to the compounded fiber/thermoplastic. Oneother method for incorporation of pesticide is to compound the fiber andthermoplastic, then add the calcium stearate and spray the pesticide onthe complete matrix prior to extrusion. All methods produced a finishedextruded profile containing the pesticide.

Make up of the extrusion composite material was performed in a batchprocess. The mixtures were prepared by weighing cellulose and fiber intobins. These bins were dumped in batches of about 80 lbs into the Gelimatfor compounding. The compounded matrix was dumped from the Gelimat ontoa conveyor, passed through a compression roller while the matrix wasstill hot to increase the bulk density of the matrix and then thismatrix was broken up into feed stock for the extruder. Multiple batchesof the same mixture were run through the Gelimat and accumulated untilextruded. Extrusion was conducted in a 65 mm Cincinnati Milacron twinscrew extruder with a short coupling to a 0.8 inch circular die. Afterexiting the die, the extruded rod was passed through a cooling chamberand the profile was cooled with sprays of chilled water. After thecooling chamber, the rod was passed into a puller after which the rodswere cut to a pre-determined size.

Table 2 below shows the composition and layout for one set of compositematerials prepared and tested.

TABLE 2 Extrusion Runs at Teel Plastics Teel Plastic, Barbaroo WisconsinRuns, Compositions and Conditions Hexaflumuron (“Hexa”) and Noviflumuron(“Novi”)as AIs Run Extrusion % % Expected Assay # Run (assay of AI onFiber) Temp. ° C. % Cellu CAB CA Stear Insecticide % % W/W 1 SolkaFlocPrill/CAB 130-135 68.6 29.4 2 Blank 2 1.6% Hexa SolkaFloc Prill/CAB130-135 68.6 29.4 2 0.63 or > 0.78 3 0.63 solid Hexa SolkaFloc Prill/CAB130-135 68.6 29.4 2 0.55 or > 0.475 4 1.6% Novi SolkaFloc Prill/CAB130-135 68.6 29.4 2 0.63 or > 0.774 5 0.63% solid Novi SolkaFlocPrill/CAB 130-135 68.6 29.4 2 0.55 or > 0.502 6 1.26% Liq Novi SolkaFlocPrill/CAB 130-135 68.6 29.4 2 0.55 or > 0.628

Batches were prepared by mixing the fiber with the CAB (a 50/50 mix ofCAB 531-1 with CAB 551-0.01) and running the batches through the Gelimatto compound the mixture. After mixing and heating in the Gelimat, thebatch was dumped onto a conveyor to a paired roller to compress thecompounded mixture. The densified mixture was passed to a cutter toproduce dry, compounded feed material for the extruder. The combinedGelimat batches were then weighed and placed in a ribbon blender whereCalcium Stearate was added. If the pesticide was to be added aftercompounding, the pesticide was mixed with the Calcium Stearate and themixture added to the compounded matrix. After mixing, the completedmatrix was fed into the twin screw extruder and extruded to produce thefinal profile. The extruded profile was cooled in a spray tank (about 30ft. long), passed through a caterpillar puller to keep the profilemoving and the profile then cut into the desired lengths.

Formulation 1 (Blank Control Pre-extrusion) was made in Run #1 bycompounding SolkaFloc prills (in Gelimat) with CAB without any pesticidepresent. After compounding, Ca stearate was added, and then the mixturewas extruded.

Formulation 2 (Hexaflumuron on Fiber) was made in Run #2 by dilutingHexaflumuron 50% concentrate (liquid) with water and spraying thediluted mixture on SolkaFloc prills.

Resulting mixture was then compounded, Ca stearate was added, and thenthe mixture was extruded.

Formulation 3 (Hexaflumuron as solid in Ca Stearate) was made in Run #3by blending solid, milled hexaflumuron technical (99+% pure) with Castearate and this mixture was blended with a compounded prill/CABmixture, then extruded.

Formulation 4 (Noviflumuron on fiber) was made in Run #4 using the sameprocess as that used to make Formulation 2, with the exception thatnoviflumuron 50% concentrate was substituted for hexaflumuron 50%concentrate.

Formulation 5 (Novi on Ca Stearate) was made in Run #5 using the sameprocess as that used to make Formulation 3, wit the exception thatmilled noviflumuron technical (99+% pure) was substituted forhexaflumuron technical.

Formulation 6 (Novi sprayed on compounded matrix) was made in Run #6 bycompounding SolkaFloc prills (in Gelimat) with CAB. Ca Stearate wasmixed with the post-compounded batch, then diluted noviflumuron 50%concentrate was spray applied. Finally the mixture was extruded.

Extruded samples were produced at Teel Plastics. The fiber and plasticwere mixed in a Gelimat, a high shear mixer for solids, to compound thefiber and plastic. The fiber and plastic are dumped into the Gelimattogether, the cycle started and the high shear mixer mixes thecomponents and melts the plastic to initiate the binding of thethermoplastic with the fiber. The high shear mixing rapidly increasesthe temperature of the mixture in the Gelimat, driving off water andmelting the plastic which binds with the fiber. The compounded matrixwas then mixed with Calcium Stearate lubricant and extruded through aCincinnati Milacron 65 m twin screw extruder. The dies used were variedand greater or less success was obtained depending on the length of thedie and the amount of movement and flow the extruding material wassubjected to as the matrix passed through the die. We found that ingeneral, the shorter the length of the die and the fewer the impedimentsto the flow, the better for extruding a profile. Incorporation of theactive ingredients was optimized in the extruder at Teel Plastics with ashort, straight through die with no impediments such as a spiders orsplitters in the die.

As discussed above, and listed in Table 1, several fibers provided byInternational Fibers have been investigated. In general, the fiberlength appears to have little effect on the profiles produced. Thelarger impact is the fiber density and form. Fiber with low bulk densityis difficult to feed and handle. The granulated material flows well andis quite easy to handle with a minimum of dusting.

Bioassays of the samples produced as described in Example 1 wereconducted to test the palatability and efficacy of the materialsproduced. The studies performed, discussed in more detail in Examples 2and 3, were standard one-way continuous no-choice and limited choiceexposure tests. The samples were divided based on active ingredient intotwo trials. The Noviflumuron samples were run for four weeks sinceNoviflumuron usually is faster acting and the Hexaflumuron samples wererun for six weeks. The extruded Noviflumuron-containing compositematerials exhibited toxicity to the termites.

The experiments described in Examples 2 and 3 demonstrate that themanufacturing process for the composite materials produce an extrudedmonitor or bait well accepted by termites. The extruded compositematerials were always much better accepted than wood in all thebioassays conducted. These studies also show it is possible toincorporate active ingredient in an extruded profile and maintaininsecticidal activity against termites.

Example Two Acceptance and Efficacy of Extruded Hexaflumuron CompositeMaterial

One-way continuous no-choice and limited exposure choice tests wereperformed to determine comparative consumption and efficacy of extrudedHexaflumuron formulations over 42 days with regard to subterraneantermite species Reticulitermes flavipes. Specifically, these testsmeasure the feeding response (consumption—mg) and resultant mortality ofReticulitermes flavipes subterranean termites in no-choice (Study #1)and 7-day limited choice-feeding (Study #2) tests to extruded compositematerial formulations containing Hexaflumuron.

Study #1—Continuous Force-Feeding (No-Choice) Exposure

Test Set-Up:

Standard one-way no-choice test. The set-up for this test is shown inFIG. 8. Study was held in Walk-in Coviron kept at 26° C. and 60% RH. Thetest included 6 reps, 100 termites/rep, held for 42 days. Three controlsof each treatment were held for weight correction.

Species:

R. flavipes

Treatments—Consumption & Survivorship Graded after 6 Weeks (42 Days)

-   -   1. Extruded Formulation 1—Blank.    -   2. Extruded Formulation 2—Hexaflumuron on Fiber, Assay=0.78%    -   3. Extruded Formulation 3—Hexaflumuron as solid in Ca Stearate,        Assay—0.475%.    -   4. Blank PTC Briquettes control.    -   5. Shatter PTC bait containing 0.5% Hexaflumuron. Shatter™ (Dow        AgroSciecnes LLC.) bait is a commercially available        alpha-cellulose bullet that includes 0.5% hexaflumuron. Shatter        bait can also be referred to as “Shatter PTC bait” because the        alpha-cellulose material included therein is referred to as        preferred textured cellulose.

As used herein, the term “Blank” is used to refer to a test materialthat does not include any hexaflumuron or any other active agent (“Al”).For example, Extruded Formulation 1 in the above list is an extrudedcomposite material that includes the identified cellulosic food materialand the identified plastic matrix, but does not include any AI.Similarly, the term “Blank PTC Briquettes control” refers to briquettesof “preferred textured cellulose” (“PTC”) that does not include any AI.

Results and Discussion for Study 1—Continuous No-Choice:

TABLE 3 Continuous Force-Feeding (No-Choice) Exposure Feeding Responseof R. flavipes to Various Bait Matrix Formulations and ResultantEfficacy after 42 days mg consumed No. Survivors/100 % CorrectedMortality after 42 days after 42 days (Compared to Extruded Treatment(mean ± SEM)* (mean ± SEM)* Formulation 1 Control)** ExtrudedFormulation 1 (Blank) 201.27 ± 33 a   41.33 ± 6.75 a — ExtrudedFormulation 2 (Hex on fiber) 140.11 ± 21.6 cd  8.0 ± 4.07 b 80.64Extruded Formulation 3 (Hex in Ca Stearate) 159.07 ± 19.3 bc 12.83 ±4.92 b 69.34 Shatter (0.5% Hex) 127.73 ± 38.1 d  14.83 ± 6.78 b 64.19Blank PTC Briquettes 169.43 ± 42.8 b    37 ± 9.14 a 10.48 Each treatmentreplicated 6 times (100 termites per rep) *Within these columns, meansfollowed by same letter are not significantly different (ANOVA + LSD;p > 0.10. SEM = Standard Error of the Mean **Corrected via Abbott'sformula

For the continuous no-choice test (results listed in Table 3), R.flavipes readily consumed the extruded bait formulations; the blankextruded bait was consumed at a rate that was significantly greater thanblank PTC. The formulations containing Hexaflumuron (Formulations 2, 3and Shatter) were consumed at a lower rate than the blank extrudedmaterial (Formulation 1) over the 42-day test, but this lowerconsumption is most likely due to the toxic effect of the Hexaflumuronin these formulations affecting the consumption rate over the 42-daytest. The formulations containing Hexaflumuron had significant mortalityvs. the controls but they were not significantly different from eachother. Numerically, Extruded Formulation 2 had the greatest correctedmortality after 42 days at 80.64% followed by extruded formulation 3 at69.34% and Shatter at 64.19%. It was noted that the surviving termitesexposed to the extruded formulations containing Hexaflumuron hadsymptoms of chitin synthesis inhibitor effects in that may appearsslow/sick and were pale in color. The surviving termites exposed to theblank extruded material appeared normal in appearance. Consistent with aprior study, the blank extruded formulation control (Formulation 1) wasconsumed significantly more than the blank PTC briquettes control andnumerically there were more survivors for the blank extruded material.

Study #2—Limited Choice Exposure

Test Set-Up:

Standard one-way paired-choice efficacy test vs. untreated southernyellow pine (SYP—½″ size). The set-up for this test is shown in FIG. 9.Study was held in Walk-in Coviron kept at 26° C. and 60% RH. The testincluded 6 reps, 100 termites/rep, held for 42 days. After 7 days, thecomposite material and the SYP were removed and replaced with blankfilter paper for the remaining duration of the test. Three controls ofeach treatment were held for weight correction.

Species:

R. flavipes

Treatments—Consumption & Survivorship Graded after 6 Weeks (42 Days)

-   1. Extruded Formulation 1—Blank.-   2. Extruded Formulation 2—Hexaflumuron on Fiber, Assay=0.78%-   3. Extruded Formulation 3—Hexaflumuron as solid in Ca Stearate,    Assay—0.475%.-   4. Blank PTC Briquettes control.-   5. Shatter PTC bait containing 0.5% Hexaflumuron.    Results and Discussion for Study 2: Limited Choice Exposure:

TABLE 4 Choice Feeding/Efficacy Test Comparative Feeding Response of R.flavipes to Various Bait Matrix Formulations and Untreated SYP after 7days, and Resultant Efficacy after 42 days % Corrected Mortality mgconsumed Palatability Ratio, mg No. Survivors/100 (Compared to after 7days Treatment ± mg after 42 days Formulation 1 Paired Choice* (mean ±SEM)* Untreated SYP (mean ± SEM)** Extruded Control){circumflex over( )} Formulation 1 25.97 ± 6.76 a  3.26 20.83 ± 6.76 a  — (Blank) vs.7.97 ± 2.87 b Untreated SYP (p value = 0.044) Formulation 2 (Hex 26.17 ±5.2 a  3.55 4.83 ± 4.83 c  76.8 on fiber) vs. 7.38 ± 32.1 b UntreatedSYP* (p value = 0.054) Formulation 3 (Hex 22.03 ± 8.33 a  5.97 8.67 ±4.11 bc 58.38 in Ca Stearate) vs. 3.69 ± 1.52 b Untreated SYP (p value =0.063) Shatter (0.5% Hex) 31.97 ± 4.41 a  5.94 11.67 ± 5.10 abc 43.9 vs.Untreated SYP 5.38 ± 2.29 b (p value = 0.008) Blank PTC 25.90 ± 5.43 a 7.87 18.5 ± 8.79 ab 11.19 Briquettes vs. 3.29 ± 1.73 b Untreated SYP (pvalue = 0.015) Each choice test replicated 6 times (100 termites perrep). *4 reps for consumption *Within each choice test, means followedby same letter are not significantly different (T-Test; p > 0.10) SEM =Standard Error of the Mean **Within this column, means followed by sameletter are not significantly different (ANOVA + LSD; p > 0.10).{circumflex over ( )}Corrected via Abbott's formula

The limited choice test results (Table 4) show that all treatments wereconsumed significantly more than SYP. The controls did not perform wellin this limited choice test. The survivorship results for this limitedchoice test were similar to what was found in the continuous no-choicetest (Table 3); the extruded formulations containing Hexaflumuron weresignificantly better than the blank extruded and numerically better thanShatter.

Results from these two tests show that the extruded Hexaflumuronformulations are readily accepted and consumed at a very high rate, andextruded formulations containing Hexaflumuron were preferred over SYP.In addition, the extruded formulations containing Hexaflumuron hadsignificantly more activity than controls and had numerically higher butstatistically similar effect compared to Shatter. Termite mortality wasnumerically higher but statistically similar for theextruded+Hexaflumuron formulations vs. Shatter bait.

Example Three Acceptance and Efficacy of Extruded Noviflumuron CompositeMaterial

One-way continuous no-choice (Study #1) and limited choice exposure(Study #2) tests were performed to determine comparative consumption andefficacy of new extruded Noviflumuron formulations over 28 days to R.falvipes. These tests were designed for the purpose of determining whatis the feeding response (consumption—mg) and resultant mortality ofReticulitermes flavipes subterranean termites in no-choice and 7-daylimited choice-feeding tests to a new extruded formulation containingNoviflumuron, thereby quantifying palatability and efficacy measurementsof new extruded composite materials containing Noviflumuron.

Study #1—Continuous Force-Feeding (No-Choice) Exposure

Test Set-Up:

Standard one-way no-choice test. Test set-up is shown in FIG. 8. Studywas held in Walk-in Coviron kept at 26° C. and 60% RH. Test included 6reps, 100 termites/rep, held for 28 days. Three controls of eachtreatment were held for weight correction.

Species:

R. flavipes

Treatments—Consumption & Survivorship was Graded after 4 Weeks (28 Days)

-   1. Extruded Formulation 1—Blank control.-   2. Extruded Formulation 4—Noviflumuron on Fiber, Assay=0.774%-   3. Extruded Formulation 5—Noviflumuron on Ca Stearate, Assay=0.502%.-   4. Extruded Formulation 6—Noviflumuron sprayed on compounded matrix,    Assay=0.628%-   5. Recruit IV PTC bait containing 0.5% Noviflumuron-   6. Blank PTC Briquettes.    Results and Discussion for Study 1—Continuous No-Choice:

TABLE 5 Continuous Force-Feeding (No-Choice) Exposure. Feeding Responseof R. flavipes to Various Bait Matrix Formulations and ResultantEfficacy after 28 days mg consumed No. Survivors/100 % correctedMortality after 28 days after 28 days (Compared to extruded Treatment(mean ± SEM)* (mean ± SEM)* Formulation 1 Control) Extruded Formulation1 (Blank) 161.39 ± 6.40 a   87 ± 1.67 a — Extruded Formulation 4 (Novion fiber) 127.95 ± 6.71 b 53.16 ± 2.70 b 38.9 Extruded Formulation 5(Novi in Ca Stearate) 134.84 ± 7.59 b 51.16 ± 3.77 b 41.2 ExtrudedFormulation 6 (Novi sprayed on 121.52 ± 7.36 b 52.83 ± 3.03 b 39.28compounded matrix) Recruit IV PTC (0.5% Novi)  47.82 ± 10.3 c  25.5 ±8.33 c 70.69 Blank PTC Briquettes 118.16 ± 2.96 b 77.83 ± 3.03 a 10.54Each treatment replicated 6 times (100 termites per rep). *Within thesecolumns, means followed by same letter are not significantly different(ANOVA + LSD; p > 0.10). SEM = Standard Error of the Mean ** Correctedvia Abbott's formula

For the continuous no-choice test (results set forth in Table 5), R.flavipes readily consumed the extruded bait formulations containingNoviflumuron at a rate that was statistically equal to that of blank PTCbriquettes. Recruit IV was consumed significantly less than the extrudedformulations, but this lower consumption is most likely due to the earlyonset of the toxic effect of the Noviflumuron in the Recruit IV bait.Recruit IV had significantly the greatest mortality after 28 days withan average of 25.5 survivors/100 with the corrected mortality=70.60%. Itwas noted that the surviving termites exposed to Recruit IV were verysick and near death. The extruded formulations containing Noviflumuron(Formulations 4, 5 & 6) all had similar activity that was significantlybetter than the controls; with the corrected mortality of the threeformulations very consistent in the 39-41% range. At 28 days, it wasnoted that some of the surviving termites exposed to the extrudedNoviflumuron formulations were slowed and showing toxic effects whilesome appeared normal. These observations were similar across the threeformulations. It was interesting to note that the blank extrudedformulation (Formulation 1) was consumed significantly more than eventhe blank PTC briquettes and numerically there were more survivors forthe blank extruded material which suggests that the extruded formulationis adequately nutritious for the termites.

Study #2—Limited Choice Exposure

Test Set-Up:

Standard one-way paired-choice efficacy test vs. untreated southernyellow pine (SYP=½″ size). Test set-up is as shown in FIG. 9. Study washeld in Walk-in Conviron kept at 26° C. and 60% RH. The test included 6reps, 100 termites/rep, held for 28 days. After 7 days, bait matrixtreatment and SYP were removed and replaced with blank filter paper forthe remaining duration of the test. Three controls of each treatmentwere held for weight correction.

Species:

R. flavipes

-   1. Extruded Formulation 1—Blank vs. SYP-   2. Extruded Formulation 4—Noviflumuron on Fiber, Assay=0.774% vs.    SYP-   3. Extruded Formulation 5—Noviflumuron on Ca Stearate, Assay=0.502%    vs. SYP-   4. Extruded Formulation 6—Noviflumuron sprayed on compounded matrix,    Assay=0.628% vs. SYP-   5. Recruit IV PTC bait containing 0.5% Noviflumuron vs. SYP-   6. Blank PTC Briquettes control vs. SYP    Results and Discussion for Study 2: Limited Choice Exposure:

TABLE 6 Choice Feeding/Efficacy Test. Comparative Feeding Response of R.flavipes to Various Bait Matrix Formulations and Untreated SYP after 7days, and Resultant Efficacy after 28 days % Corrected Mortality mgconsumed Palatability Ratio, mg No. Survivors/100 (Compared to after 7days Treatment + mg after 28 days Formulation 1 Paired Choice* (mean ±SEM)* Untreated SYP (mean ± SEM)** Extruded Control){circumflex over( )} Formulation 1 52.02 ± 2.39 a  ∘∘   63 ± 5.46 a — (Blank) vs. 0.00 ±0.00 b Untreated SYP (p value < 0.0001) Formulation 4 39.0 ± 5.2 a 0.965 29.66 ± 4.25 b 52.93 (Novi on fiber) vs. 40.4 ± 32.1 a UntreatedSYP (p value = 0.965) Formulation 5 44.9 ± 2.60 a 2.47  31.5 ± 2.62 b 50(Novi on CA Stearate) vs. 18.2 ± 11.7 b Untreated SYP (p value = 0.090)Formulation 6 48.66 ± 6.24 a  199 30.83 ± 2.69 b 51.06 (Novi sprayed on)vs. 0.24 ± 0.24 b Untreated SYP (p value = 0.001) Recruit IV PTC 50.08 ±5.03 a  6.25  1.67 ± 1.67 c 97.35 (0.5% Novi) vs. 8.01 ± 8.01 bUntreated SYP (p value = 0.016) Blank PTC 63.63 ± 6.95 a  ∘∘  57.8 ±8.68 a 8.25 Briquettes vs. 0.00 ± 0.00 b Untreated SYP (p value <0.0001) *Each choice test replicated 6 times (100 termites per rep)*Within each choice test, means followed by same letter are notsignificantly different (T-Test; p > 0.10). SEM = Standard Error of theMean **Within this column, means followed by same letter are notsignificantly different (ANOVA + LSD; p > 0.10). {circumflex over( )}Corrected via Abbott's formula

The limited choice rest results (Table 6) show that all treatments wereconsumed significantly more than SYP except for Formulation 4. It isbelieved that the high SYP consumption (40.4 mg) and the high StandardError of the Mean (SEM) of 32.1 in this choice comparison is an errorcaused when drying the samples in the oven. A few of the SYP samplesvisibly lost an excessive amount of sap during the oven drying, whichlikely resulted in the higher SEM. In addition, when examining the SYPsamples there appeared to be little to no visible consumption.Survivorship results for the treatments were similar to what we saw withthe continuous no-choice test (Recruit IV>extruded Noviflumuronformulations>controls); however overall more termites died in this studyacross all of the treatments including the controls. Two different R.flavipes colonies were used in the limited choice test than what wereused in the continuous no-choice test and colony differences are mostlikely the reason for the lower overall survivorship in this limitedchoice test. The condition of the survivors were visibly similar to whatwe saw with the continuous no-choice test; the Recruit IV survivors werenear death while some of the extruded Noviflumuron survivors werevisibly slow and affected while some appear normal. Again, these visibleeffects were noted similarly across the three extruded treatments.

Results from these two tests show that the extruded Noviflumuronformulations are readily accepted and consumed at a very high ratesimilar to blank PTC. The extruded composite materials gave significantactivity vs. the control but were less active than Recruit IV containing0.5% Noviflumuron at 28 days. The three extruded Noviflumuronformulations were statistically similar for efficacy across the twotests and all had significant activity vs. the controls. The loweractivity at 28 days is most likely due to bioavailability of theNoviflumuron in the extruded formulations. Improved formulations thatare more bioavailable will be expected to achieve activity similar toRecruit IV.

Example Four Production of Extruded Composite Materials (Run 2)

A second set of composite material batches were prepared using the samestarting materials as described in Example 1. Table 7 below shows thecomposition and layout for the second set of composite materialsprepared.

TABLE 7 Extru Wt. Wt. Run # Run (assay of AI on Fiber) Temp. ° C. Cellu% Cellu % CAB CAB 7 SolkaFloc Prill/CAB 130-135 68.6 480.20 29.4 205.8Blank Run Modified L Die 8 0.86% Novi SolkaFloc Prill/ 130-135 68.61577.80 29.4 676.2 CAB Noviflumuron sprayed on Cellulose Modified L Die9 0.85% Hex SolkaFloc Prill/ 130-135 68.6 192.08 29.4 82.32 CABHexaflumuron sprayed on cellulose Modified L Die Batch Ca Wt Prod'n SizeNum of Run # Stear Lub Rate ft/min Expected % Assay Lbs. Max Ft. Parts 72 14 10 to 15 Blank 0 700 1951.4 1672.63 Tested 8 2 46 10 to 15 0.50.79% at 2300  6411.75 5495.79 Early part of Run Tested 9 2 5.6 10 to 150.5 0.58% 280 780.561 669.053 Tested

The extruded composite materials produced in Runs 7-9 are referred toherein as Formulations 7-9, respectively. Bioassays of theseFormulations 7-9 were conducted, as discussed in greater detail inExamples 5-9, below.

Example Five Acceptance and Efficacy of Extruded Hexaflumuron CompositeMaterials to Two Subterranean Termite Species

Efficacy of extruded Hexaflumuron treatment formulations as described inExample 4 (Spray on Cellulose Formulation) to R. flavipes & C.formosanus were tested.

Test Set-Up:

Standard One-way no-choice efficacy test with cups, 4 or 6 reps of 100termites/rep held for 28, 42 or 56 days. All studies were held inWalk-in Conviron at 26° C. and 60% RH. Three controls of each treatmentwere held for weight correction.

Species:

R. flavipes and C. formosanus (2 colonies of each species used in eachtest)

Treatments—Consumption & Survivorship was Graded at 6 Weeks (42 Days):

-   1. Extruded Formulation 7—Blank-   2. Extruded Formulation 9—Hexaflumuron Sprayed on Cellulose,    Assay=0.58%-   3. Shatter PTC bait containing 0.5% Hexaflumuron    Each test was replicated 6 times with 100 termites per replicate.    Thus, three no-choice tests×six reps=18 one-way units and 1800    termites (R. flavipes & C. formosanus) were installed for each    species. Therefore, for 2 species, 36 one-way units and 3600    termites were required    Results:

Results are set forth in Tables 8 (R. flavipes) & 9 (C. formosanus).

TABLE 8 Continuous Force-Feeding (No-Choice) Exposure. Feeding Responseof R. flavipes to Various Bait Matrix Formulations ContainingHexaflumuron and Resultant Efficacy after 42 days. % Corrected Mortalitymg consumed No. Survivors/100 (Compared to Extruded after 42 days after42 days Formulation 7 Treatment (mean ± SEM)* (mean ± SEM){circumflexover ( )} Blank Control)** Extruded Formulation 7 - Blank 343.3 ± 22.8 a86.67 ± 2.92 a  — Extruded Formulation 9 Hexaflumuron - 207.0 ± 11.9 b9.67 ± 2.50 b 88.84 Sprayed on cellulose, Assay = 0.58% Shatter PTC baitcontaining 0.5% 126.0 ± 10.0 c 3.33 ± 2.06 c 96.16 Hexaflumuron Eachtreatment replicated 6 times (100 termites per rep). *For Consumption,means followed by same letter are not significantly different, (ANOVA +LSD; p > 0.10). {circumflex over ( )}For Survivors, means followed bythe same letter are not significantly different, (Binary LogisticRegression). **Corrected via Abbott's formula

TABLE 9 Continuous Force-Feeding (No-Choice) Exposure. Feeding Responseof C. formosanus to Various Bait Matrix Formulations ContainingHexaflumuron and Resultant Efficacy after 42 days. % Corrected Mortalitymg consumed No. Survivors/100 (Compared to Extruded after 42 days after42 days Formulation 7 Treatment (mean ± SEM)* (mean ± SEM){circumflexover ( )} Blank Control)** Extruded Formulation 7 - Blank 90.12 ± 19.0 a65.67 ± 2.91 a — Extruded Formulation 9 Hexaflumuron - 99.68 ± 13.9 a59.67 ± 2.33 a 9.14 Sprayed on cellulose, Assay = 0.58% Shatter PTC baitcontaining 0.5% 52.35 ± 0.58 b 44.67 ± 2.33 b 31.97 Hexaflumuron Eachtreatment replicated 3 times (100 termites per rep). 3 additional repswere omitted due to a bad (sick) colony. *For Consumption, meansfollowed by same letter are not significantly different, (ANOVA + LSD;p > 0.10). {circumflex over ( )}For Survivors, means followed by thesame letter are not significantly different, (Binary LogisticRegression). **Corrected via Abbott's formula

Similar to what was seen previously, R. flavipes actively fed on theextruded formulations with consumption of the extruded formulationcontaining hexaflumuron (Formulation 9) significantly greater thanShatter. Although mortality was significantly less for the extrudedsprayed on cellulose formulation (Formulation 9) in comparison toShatter, overall corrected control for Formulation 9 was high at 88.84%which was just slightly lower in comparison to Shatter at 96.16% at timeof study conclusion (42 days). Control to R. flavipes was greater inthis test compared to what was seen previously and this may be due tothe higher percentage of hexaflumuron (0.58%) or possibly termite colonydifferences. Shatter also had greater efficacy in this study which couldbe a related to variation of different termite colonies or possibly thetime of year these tests were run (this study was run mid-latespring/early summer vs. late winter/early spring for earlier study).Trends for C. formosanus (Table 9) were similar to what we sawpreviously with findings for extruded noviflumuron formulations. Feedingon the extruded formulation with hexaflumuron was greater than Shatter;however Shatter efficacy was significantly higher. Overall efficacy waslow for this study and it may have been better to let the study golonger, but a decision was made to break down at 42 days due to the factthat the control was starting to drop off which does happen on occasionduring these longer term lab studies.

Example Six Acceptance and Efficacy of Extruded Noviflumuron CompositeMaterials to Two Subterranean Termite Species

Efficacy of extruded Noviflumuron treatment formulations (Higher AssaySpray on Cellulose Formulation) to R. flavipes & C. formosanus weretested.

Test Set-Up:

Standard One-way no-choice efficacy test with cups, 4 or 6 reps of 100termites/rep held for 28, 42 or 56 days. All studies were held inWalk-in Conviron at 26° C. and 60% RH. Three controls of each treatmentwere held for weight correction. Study #1 was a 6-week test and Study #2was an 8-week test.

Species:

R. flavipes and C. formosanus (2 colonies of each species used in eachtest)

Treatments (all Tests)—Consumption & Survivorship was Graded after 6Weeks (42 Days) for Study #1 and 8 Weeks (56 Days) for Study #2:

-   1. Extruded Formulation 7—Blank-   2. Extruded Formulation 8 sprayed on cellulose—Noviflumuron 0.79%-   3. Recruit IV PTC containing 0.5% Noviflumuron    Each test was replicated 6 times with 100 termites per replicate.    For all tests combined, 6 (3 treatments×2 tests/treatment) no-choice    set ups×6 reps=36 one-way units with cups and 3600 termites of each    species were set-up. Therefore for 2 species, 72 one-way units with    cups and 7200 termites total were required.    Results:

Results for R. flavipes (Table 10) show that the higher assay spray onformulation (0.79% noviflumuron) had greater consumption than Recruit IVfor both the 42 day and 56 day studies and also efficacy was similar at42 days (65.77% vs 69.48%, NSD, Binary Logistic Regression) and justslightly lower; 87.58% vs. 100% corrected control for Recruit IV at 56days, however this difference was significant (Binary LogisticRegression).

TABLE 10 Continuous Force-Feeding (No-Choice) Exposure. Feeding Responseof R. flavipes to Various Bait Matrix Formulations ContainingNoviflumuron and Resultant Efficacy after 42 & 56 days. % CorrectedMortality mg consumed No. Survivors/100 (Compared to Extruded Treatmentafter 42 days after 42 days Formulation 7 (42 day Test) (mean ± SEM)*(mean ± SEM){circumflex over ( )} Blank Control)** Extruded Formulation7 - Blank 265.04 ± 14.6 a 80.83 ± 4.48 a — Extruded Formulation 8Noviflumuron - 141.93 ± 10.6 b 27.67 ± 4.35 b 65.77 Sprayed oncellulose, Assay = 0.79% Recruit IV bait containing 0.5% 105.72 ± 7.94 c24.67 ± 7.15 b 69.48 Noviflumuron % Corrected Mortality mg consumed No.Survivors/100 (Compared to Extruded Treatment after 56 days after 56days Formulation 7 (56 day Test) (mean ± SEM)* (mean ± SEM){circumflexover ( )} Blank Control)** Extruded Formulation 7 - Blank 324.8 ± 22.2 a83.17 ± 5.02 a — Extruded Formulation 8 - Noviflumuron - 161.5 ± 13.2 b10.33 ± 2.33 b 87.58 Sprayed on cellulose, Assay = 0.79% Recruit IV baitcontaining 0.5% 79.84 ± 10.7 c  0.00 ± 0.00 c 100 Noviflumuron Eachtreatment replicated 6 times (100 termites per rep). *For Consumption,means followed by same letter are not significantly different, (ANOVA +LSD; p > 0.10). {circumflex over ( )}For Survivors, means followed bythe same letter are not significantly different, (Binary LogisticRegression) **Corrected via Abbott's formula

Also similar to what was found in the studies completed previously, theconsumption by C. formosanus was significantly more for the extrudedformulations in comparison to Recruit IV, but the corrected mortalitycompared to control was significantly lower for Extruded Formulation 8(assay=0.79% noviflumuron sprayed on cellulose) with results at 0% forFormulation 8 vs. 48.21% for Recruit IV at 42 days and 31.99% forFormulation 8 vs. 85.14% for Recruit IV (Table 11). These lab resultsagain are indicative of what has been recently reported fromexperimental field trials with extruded materials to C. formosanus.

TABLE 11 Continuous Force-Feeding (No-Choice) Exposure. Feeding Responseof C. formosanus to Various Bait Matrix Formulations ContainingNoviflumuron and Resultant Efficacy after 42 & 56 days. % CorrectedMortality mg consumed No. Survivors/100 (Compared to Extruded Treatmentafter 42 days after 42 days Formulation 7 (42 day Test) (mean ± SEM)*(mean ± SEM)* Blank Control)** Extruded Formulation 7 - Blank 75.18 ±17.1 a 74.67 ± 6.06 a — Extruded Formulation 8 - Noviflumuron - 52.55 ±10.7 a 78.33 ± 2.96 a 0.0 Sprayed on cellulose, Assay = 0.79% Recruit IVbait containing 0.5% 14.53 ± 2.98 b 38.67 ± 15.6 b 48.21 Noviflumuron %Corrected Mortality mg consumed No. Survivors/100 (Compared to ExtrudedTreatment after 56 days after 56 days Formulation 7 (56 day Test) (mean± SEM)* (mean ± SEM)* Blank Control)** Extruded Formulation 7 - Blank103.01 ± 25.1 a  74.0 ± 4.16 a — Extruded Formulation 8 - Noviflumuron - 36.64 ± 20.7 b 50.33 ± 6.33 b 31.99 Sprayed on cellulose, Assay = 0.79%Recruit IV bait containing 0.5% 25.19 ± 3.8 b 11.00 ± 5.86 c 85.14Noviflumuron Each treatment replicated 3 times (100 termites per rep). 3additional reps were omitted due to a bad (sick) colony. *ForConsumption, means followed by same letter are not significantlydifferent, (ANOVA + LSD; p > 0.10). {circumflex over ( )}For Survivors,means followed by the same letter are not significantly different,(Binary Logistic Regression) **Corrected via Abbott's formula

Overall for both R. flavipes and C. formosanus, the extrudedformulations containing either hexaflumuron or noviflumuron weregenerally consumed significantly more than Shatter and Recruit IV. Thiswas true for both the sprayed on cellulose and the incorporated in thecellulose extruded formulations. Differences in consumption between thetwo extruded formulations were not much different for either species;however R. flavipes numerically consumed more extruded material vs. C.formosanus when comparing the different tests. Depending on the test,average consumption of one of the extruded formulations may have beenmore at one evaluation and then in the same test when graded for adifferent time period (i.e., 42 days vs 56 days) the other extrudedformulation may have been consumed more—there was no clear preferencebetween the formulations (sprayed on cellulose vs. incorporated incellulose for either species.

Mortality was most often significantly less (Binary Logistic Regressionanalysis) for the extruded formulations of hexaflumuron vs. Shatter andnoviflumuron vs. Recruit IV. This was especially true for C. formosanuswhere control was much less (highly significant) than Shatter or RecruitIV. For R. flavipes, the differences were not as great and in a fewtests, the efficacy was not significantly different vs. Shatter orRecruit IV.

Example Seven Acceptance and Efficacy of Extruded Noviflumuron andHexaflumuron Composite Materials to Multiple Subterranean TermiteSpecies

Palatability and efficacy of extruded AI-containing composite materialsto multiple different termite species was tested to determine whetherthe key subterranean termite species Reticulitermes virginicus, C.formosanus, Reticulitermes Hesperus, Reticulitermes speratus andHeterotermes aureus consume (mg) less (p=0.1) of the extrudedformulations containing the AIs noviflumuron or hexaflumuron compared tocommercial AI-containing baits in no-choice laboratory tests, and todetermine whether extruded formulations containing the AIs noviflumuronor hexaflumuron cause significantly less mortality vs. the commercialbaits (p=0.05, Binary Logistic Regression) to key subterranean termitespecies Reticulitermes virginicus, C. formosanus, ReticulitermesHesperus, Reticulitermes speratus and Heterotermes aureus in no-choicelaboratory tests. The tests comparing extruded composite materialscontaining noviflumuron to Recruit IV examined data at 4, 6 and 8 weeks.The tests comparing extruded composite materials containing hexaflumuronto Shatter bait examined data at 6 weeks.

Study #1: Consumption & Efficacy of Extruded Noviflumuron Formulationsto Additional Termite Species

Species:

R. virginicus, C. formosanus, R. hesperus, H. aureus

Test Set-Up:

One-way, continuous no-choice tests, 4-8 reps, 100 termites per rep, 4and/or, 6 and/or, 8-week data (R. virginicus & C. formosanus=4, 6, & 8week data; R. hesperus & H. aureus=6 week data only)

Treatments

-   1. Extruded Formulation 1—Blank-   2. Extruded Formulation 4—Novi on fiber*, 0.774%-   3. Extruded Formulation 5—Novi on Ca Stearate, 0.502%-   4. Extruded Formulation 6—Novi sprayed on compounded matrix**,    0.628%-   5. Recruit IV PTC bait containing 0.5% noviflumuron-   6. Blank PTC Briquettes control    -   *=sprayed on cellulose powder, compacted and then broken into        prills (granules or pellets)    -   **=pre-formed prills (granules or pellets) sprayed on with        active        Notes: For C. formosanus, Formulation 4 was not tested as no        more material was available. For R. hesperus & H. aureus, only        Formulations 1, 2 and 5 were tested due to low termite        availability.        Feeding response data for species R. Virginicus are set forth in        Table 12 below:

TABLE 12 Study 1: Continuous Force-Feeding (No-Choice) Exposure/EfficacyTest. Feeding Response of R. virginicus to Extruded Bait MatrixFormulations containing Noviflumuron after 28, 42 and 56 days. mgconsumed mg consumed mg consumed after 28 days after 42 days after 56days Treatment (mean ± SEM)* (mean ± SEM)* (mean ± SEM)* ExtrudedFormulation 1 (Blank) 70.93 ± 12.3 a  122.94 ± 6.8 a  108.63 ± 22.9 a Extruded Formulation 4 (0.774% Novi on fiber) 40.04 ± 14.6 bc  53.32 ±10.7 ab  46.28 ± 10.9 bc Extruded Formulation 5 (0.502% Novi in CaStearate) 48.63 ± 12.1 ab 80.82 ± 12.4 a 65.37 ± 13.1 b ExtrudedFormulation 6 (0.628% Novi sprayed 33.76 ± 12.4 bc 58.35 ± 9.9 c   40.95± 14.2 bc on compounded matrix) Recruit IV PTC (0.5% Novi) 16.19 ± 1.7c  19.4 ± 1.9 b 15.69 ± 2.65 c Blank PTC Briquettes 68.15 ± 8.4 a  77.85± 14.2 a 54.17 ± 11.4 b Each treatment replicated 4 times (100 termitesper rep). *Within each columns, means followed by same letter are notsignificantly different (ANOVA + LSD; p > 0.10). 28, 42, and 56 dayreadings from 3 separate tests. SEM = Standard Error of the Mean

Survivorship data at 4 weeks, 6 weeks and 8 weeks for R. Virginicus areset forth in FIGS. 10, 11 and 12, respectively.

Feeding response data for species C. formosanus are set forth in Table13 below:

TABLE 13 Study 1: Continuous Force-Feeding (No-Choice) Exposure/EfficacyTest. Feeding Response of C. formosanus to Extruded Bait MatrixFormulations containing Noviflumuron after 28, 42 and 56 days. mgconsumed mg consumed mg consumed after 28 days after 42 days after 56days Treatment (mean ± SEM)* (mean ± SEM)* (mean ± SEM)* ExtrudedFormulation 1 (Blank) 102.33 ± 9.88 a  114.04 ± 38.2 a  173.37 ± 69.4 a Extruded Formulation 4 (0.774% Novi on fiber) 60.64 ± 5.11 c   71.49 ±4.23 ab  31.31± 28.1 c Extruded Formulation 5 (0.502% Novi in CaStearate) 83.94 ± 5.02 ab 113.81 ± 6.8 a  125.22 ± 35.6 b  Recruit IVPTC (0.5% Novi) 27.36 ± 2.03 d  30.85 ± 2.92 b 27.93 ± 14.2 c Blank PTCBriquettes 63.70 ± 15.9 bc 94.85 ± 1.97 a 96.95 ± 55.9 b Each treatmentreplicated 4 times (100 termites per rep). *Within each columns, meansfollowed by same letter are not significantly different (ANOVA + LSD;p > 0.10). 28, 42, and 56 d readings from 3 separate tests. SEM =Standard Error of the Mean

Survivorship data at 4 weeks, 6 weeks and 8 weeks for C. formosanus areset forth in FIGS. 13, 14 and 15, respectively.

Feeding response data for species Heterotermes aureus are set forth inTable 14 below:

TABLE 14 Study 1: Continuous Force-Feeding (No-Choice) Exposure/EfficacyTest. Feeding Response of Heterotermes aureus to Extruded Bait MatrixFormulations containing Noviflumuron after 42 days. mg consumed after 42days Treatment (mean ± SSEM)* Extruded Formulation 1 (Blank) 60.40 ± 7.1a Extruded #4 (Novi on fiber, 0.774%) 15.07 ± 3.2 b Recruit IV PTC (0.5%Novi)  3.96 ± 0.75 c Each treatment replicated 8 times (100 termites perrep) *Within column, means followed by same letter are not significantlydifferent (ANOVA + LSD; p > 0.10). SEM—Standard Error of the Mean

Survivorship data at 6 weeks for Heterotermes aureus are set forth inFIG. 16.

Feeding response data for species Reticulitermes hesperus are set forthin Table 15 below:

TABLE 15 Study 1: Continuous Force-Feeding (No-Choice) Exposure/EfficacyTest. Feeding Response of Reticulitermes hesperus to Extruded BaitMatrix Formulations containing Noviflumuron after 42 days (6 weeks). mgconsumed after 42 days Treatment (mean ± SEM)* Extruded Formulation 1(Blank) 136.67 ± 15.4 a  Extruded Formulation 4 (Novi on fiber, 0.774%)36.42 ± 10.0 b Recruit IV PTC (0.5% Novi) 14.69 ± 4.06 c Each treatmentreplicated 8 times (100 termites per rep). *Within this column, meansfollowed by same letter are not significantly different (ANOVA + LSD;p > 0.10). SEM = Standard Error of the Mean

Survivorship data at 6 weeks for Reticulitermes hesperus are set forthin FIG. 17.

In addition to the above, similar tests were conducted in Japan to testthe consumption and efficacy of noviflumuron-containing extrudedcomposite materials to subterranean termite species R. speratus. Resultsof these tests (data not shown) revealed that R. speratus consumed moreextruded composite material compared to Recruit IV in the no-choice labtests at 4 weeks and 6 weeks and that the number of survivors afterexposure to the noviflumuron-containing extruded composite material wasgreater than that of Recruit IV, but less than controls.

Study #2: Consumption & Efficacy of Extruded Hexaflumuron Formulationsto Additional Termite Species

Species:

R. virginicus, C. formosanus, R. hesperus, H. aureus

Test Set-Up:

One-way, continuous no-choice tests, 4-7 reps, 100 termites per rep, 6and/or 10-week data (C. formosanus only)

Treatments

-   1. Extruded Formulation 1—Blank-   2. Extruded Formulation 2*—0.78% Hex on Fiber-   3. Extruded Formulation 3-0.475% Hex in Ca Stearate-   4. Shatter bait containing 0.5% Hexaflumuron-   5. Blank PTC pellets control    -   *=sprayed on cellulose powder, compacted and then broken into        prills (granules or pellets)        Notes: For R. hesperus & H. aureus, only Formulations 1, 2 and 4        were tested due to low termite availability.

Feeding response data for species Reticulitermes virginicus are setforth in Table 16 below:

TABLE 16 Study 2: Continuous Force-Feeding (No-Choice) Exposure/EfficacyTest. Feeding Response of Reticulitermes virginicus to Extruded BaitMatrix Formulations containing Hexaflumuron after 42 days (6 weeks). Mgconsumed after 10 weeks Treatment (mean ± SEM)* Extruded Formulation 1(Blank) 99.43 ± 17.0 a Extruded Formulation 2 (Hex on fiber, 0.78%)81.01 ± 7.93 b Extruded Formulation 3 (Hex in Ca Stearate 0.475%) 76.50± 6.09 a Blank PTC 67.57 ± 17.8 a Shatter 46.29 ± 3.60 a Each treatmentreplicated 6 times (100 termites per rep) *Within this column, meansfollowed by same letter are not significantly different (ANOVA + LSD;p > 0.10). SEM = Standard Error of the Mean

Survivorship data at 6 weeks for Reticulitermes virginicus are set forthin FIG. 18.

Feeding response data for species Coptotermes formosanus are set forthin Table 17 below:

TABLE 17 Study 2: Continuous Force-Feeding (No-Choice) Exposure/EfficacyTest. Feeding Response of Coptotermes formosanus to Extruded Bait MatrixFormulations containing Hexaflumuron after 10 weeks. mg consumed after10 weeks Treatment (mean ± SEM)* Extruded Formulation 1 (Blank) 194.24 ±10.1 a Extruded Formulation 2 (Hex on fiber, 0.78%) 147.61 ± 8.01 bExtruded Formulation 3 (Hex in Ca Stearate, 0.475%) 185.90 ± 9.37 a Eachtreatment replicated 6 times (100 termites per rep). *Within thiscolumn, means followed by same letter are not significantly different(ANOVA + LSD; p > 0.10). SEM = Standard Error of the Mean

Survivorship data at 10 weeks for Coptotermes formosanus are set forthin FIG. 19.

Feeding response data for species Heterotermes aureus are set forth inTable 18 below:

TABLE 18 Study 2: Continuous Force-Feeding (No-Choice) Exposure/EfficacyTest. Feeding Response of Heterotermes aureus to Extruded Bait MatrixFormulations containing Hexaflumuron after 45 days (6+ weeks). mgconsumed after 10 weeks Treatment (mean ± SEM)* Extruded Formulation 1(Blank) 44.27% ± 10.7 a   Extruded Formulation 2 (Hex on fiber, 0.78%)35.65 ± 7.75 a Shatter (0.5% Hexaflumuron) 32.26 ± 4.06 a Each treatmentreplicated 7 times (100 termites per rep). *Within this column, meansfollowed by same letter are not significantly different (ANOVA + LSD;p > 0.10). SEM = Standard Error of the Mean

Survivorship data at 45 days for Heterotermes aureus are set forth inFIG. 20.

Feeding response data for species Reticulitermes hesperus are set forthin Table 19 below:

TABLE 19 Study 2: Continuous Force-Feeding (No-Choice) Exposure/EfficacyTest. Feeding Response of Reticulitermes hesperus to Extruded BaitMatrix Formulations containing Hexaflumuron after 42-d (6 weeks). mgconsumed after 10 weeks Treatment (mean ± SEM)* Extruded Formulation 1(Blank) 82.17 ± 16.2 a Extruded Formulation 2 (Hex onfibger, 0.78%)53.76 ± 14.9 b Shatter (0.5% Hexaflumuron) 62.88 ± 16.7 b Each treatmentreplicated 7 times (100 termites per rep). *Within this column, meansfollowed by same letter are not significantly different (ANOVA + LSD;p > 0.10). SEM = Standard Error of the Mean

Survivorship data at 6 weeks for Reticulitermes hesperus are set forthin FIG. 21.

As shown by the data set forth above, key subterranean termite speciesR. virginicus, C. formosanus, R. hesperus and H. aureus consume (mg)more (p=0.1) of the extruded formulations containing noviflumuron andcompared to Recruit IV in no-choice laboratory tests at 4, 6 and 8weeks, and subterranean termite species R. virginicus, C. formosanus, R.hesperus and H. aureus consume (mg) more (p=0.1) of the extrudedformulations containing hexaflumuron compared to Shatter in no-choicelaboratory tests at 6 weeks. While composite materials containingnoviflumuron generally cause less mortality vs. Recruit IV to thesubterranean termite species tested in no-choice laboratory tests at 4,6 and 8 weeks, the composite materials containing noviflumuron did causemore mortality than controls, indicating that the extruded compositematerials are an effective manner of delivering this AI to termites.Extruded composite materials containing hexaflumuron caused similarlevels of mortality vs. Shatter (p=0.05, Binary Logistic Regression) tosome of the subterranean termite species tested in no-choice laboratorytests at 6 weeks. While the extruded composite materials containinghexaflumuron caused less mortality than Shatter to other termitespecies, the hexaflumuron-containing extruded composite materials didcause higher levels of mortality than controls to these species,indicating that the extruded composite materials are an effective mannerof delivering this AI to termites.

Example Eight Trophallaxis Transfer of Extruded Pesticide CompositeMaterials

Extruded AI-containing composite materials were compared to commercialAI-containing bait materials to determine if they cause significantmortality to R. favipes in trophallaxis transfer studies at 6 and/or 8weeks post exposure.

Species:

R. favipes

Test Set-Up:

Step 1: Exposure to Extruded Material—One-way Continuous No-ChoiceSet-up

6 reps of each treatment per test

Test 1=6 weeks

Test 2=8 weeks

50 termites/rep, and held for 7 days

Step 2: Set-Up of 6 & 8 Week Tests:

From Step 1 take 6 reps/treatment and replace extruded material with0.5″×1″ MD-499 piece.

For each rep/treatment add 50 non-exposed termites (from same colonytub) for 100 termite total/rep.

6 reps, 100 termites/rep, held for 42 days (6 weeks).

Additional 6 reps, 100 termites/rep, held for 56 days (8 weeks).

Treatments:

Noviflumuron Study

-   1. Extruded Formulation 1—Blank-   2. Extruded Formulation 4—Noviflumuron on fiber, Assay=0.774%-   3. Extruded Formulation 5—Noviflumuron on Ca Stearate, Assay=0.502%-   4. Recruit IV PTC bait containing 0.5% Noviflumuron-   5. Blank PTC Briquettes control    Hexaflumuron Study-   1. Extruded Formulation 1—Blank-   2. Extruded Formulation 2—Hexaflumuron on Fiber, Assay=0.78%-   3. Extruded Formulation 3—Hexaflumuron as solid in Ca Stearate,    Assay=0.475%-   4. Blank PTC Briquettes control-   5. Shatter PTC bait containing 0.5% Hexaflumuron

The data obtained from the trophallaxis study is set forth in FIGS. 22,23, 24 and 25, in which FIGS. 22 and 23 are graphs of the number ofsurvivors for each type of material tested in the noviflumuron study at6 weeks and 8 weeks, respectively, and FIGS. 24 and 25 are graphs of thenumber of survivors for each type of material tested in the hexaflumuronstudy at 6 weeks and 8 weeks, respectively. The data set forth in FIGS.22-25 show that both Noviflumuron and Hexaflumuron 50:50 trophallaxistransfer studies over 7 days and followed out for 6 and 8 weeks hadsignificant mortality in the treatments vs. blanks.

Example Nine Acceptance and Efficacy of Extruded Pesticidal CompositeMaterials Including Spinosad and Fipronil

Tests were conducted to determine if extruded composite materialsincluding fast-acting AIs (Spinosad and Fipronil) cause significant highmortality vs. control (p=0.05, Binary Logistic Regression) to R.flavipes and C. curvignathus. Extruded materials used in this study weremade as described above, with the exception that the AI included in theextrusion was Spinosad or Fipronil as follows: Formulation 10 includes0.05% Spinosad, Formulation 11 includes 0.01% Fipronil, Formulation 12includes 0.03% Fipronil, Formulation 13 includes 0.05% Fipronil andFormulation 14 includes 0.1% Fipronil,

Species:

R. flavipes and C. curvignathus

R. flavipes (Two Tests)

Test Set-Up:

Standard One-way no-choice and choice tests (vs, SYP) 6 reps, 100termites/rep, held for 14 d. Two colonies of R. flavipes used.

Treatments (Both Tests):

-   1. Extruded Formulation 7 (Blank)-   2. Extruded Formulation 10 (0.05% Spinosad)-   3. Extruded Formulation 11 (0.01% Fipronil)-   4. Extruded Formulation 12 (0.03% Fipronil)-   5. Extruded Formulation 13 (0.05% Fipronil)-   6. Extruded Formulation 14 (0.1% Fipronil)

The results of these tests are set forth in FIGS. 26, 27 and 28, inwhich FIG. 26 sets forth results with respect to consumption of theextruded composite materials by R. Flavipes at 14 days in the no-choicetest, FIG. 27 sets forth survivorship results at 14 days in theno-choice test and FIG. 28 sets forth the results of the survivorshiptest at 14 days in the choice v. SYP test. As shown by these results,extruded composite materials including the fast-acting AIs Spinosad andFipronil cause significant high mortality vs. control to R. flavipesafter two weeks in laboratory choice and no-choice tests.

C. curvignathus Test

Test Set-Up:

One-way no choice consumption and efficacy, 4 replicates per treatment.Assessment at 7-day post-treatment.

Treatments:

-   1. Extruded Formulation 10 (0.05% spinosad)-   2. Extruded Formulation 11 (0.01% fipronil)-   3. Extruded Formulation 12 (0.03% fipronil)-   4. Extruded Formulation 13 (0.05% fipronil)-   5. Extruded Formulation 14 (0.1% fipronil)

Extruded bait consumption data of C. curvignathus after 7 days isprovided below in Table 20.

TABLE 20 Treatment Mean ± S.D. (mg) Rubber wood (untreated) 11.65 ±12.42 Formulation 10 (0.05% spinosad) 2.58 ± 1.10 Formulation 11 (0.01%fipronil) 6.75 ± 6.83 Formulation 12 (0.03% fipronil) 3.88 ± 6.17Formulation 13 (0.05% fipronil)  4.28 ± 11.55 Formulation 14 (0.1%fipronil) 5.63 ± 6.35

Percent survival data of the worker termite of C. curvignathus at 7 daysis provided below in Table 21.

TABLE 21 Treatment Mean (%) Rubber wood (untreated) 100 Formulation 10(0.05% spinosad) 46.5 Formulation 11 (0.01% fipronil) 0 Formulation 12(0.03% fipronil) 0 Formulation 13 (0.05% fipronil) 0 Formulation 14(0.1% fipronil) 25.5

Mortality is achieved mostly within 1-2 days upon introduction of bait.Spinosad bait is the only treatment where some sand/vermiculiteparticles were observed at the foraging chamber, and some termiterefused to cross over to the foraging chamber, possibly indicatingpossibly some deterrence. All termite were killed in the chambercontaining fipronil bait (Formulation 11, Formulation 12 & Formulation13) except Formulation 14 (25% survivorship). As seen from the above,extruded composite materials including the fast acting AIs Spinosad andFipronil cause high mortality vs. control to C. curvignathus after oneweek in the laboratory no-choice test.

Example Ten Termite Colony Elimination Study

Field tests were performed to determine if extruded noviflumuron and/orhexaflumuron bait matrix eliminate subterranean termite colonies whenplaced in active in-ground SENTRICON® stations, and to determine theamount of time and quantity of bait consumption needed to effect colonyelimination. Extruded materials used in this study were made asdescribed above and provided in the form of rods each having a mass ofabout 75 grams. The materials used in this test are the following:Formulation 15 rods include 0.58% Hexaflumuron and Formulation 16 rodsinclude 0.78% Noviflumuron.

Test Set-Up:

Termite colonies were exposed to AI-containing extruded compositematerial rods having a mass of about 75 grams. As a point of reference,Recruit IV bait tubes have a mass of about 65 grams.

Termite Species Tested:

R. flavipes (RETIFL), R. hageni (RETIHA), C. formosanus (COPTFO), R.virginicus (RETIVI) and R. Hesperus (RETIHE).

Treatments:

-   -   1. Formulation 15 0.58% Hexaflumuron Rods (extruded bait matrix)    -   2. Formulation 16 0.78% Noviflumuron Rods (extruded bait matrix)        Results/Discussion:

Table 22 sets forth data regarding each of the 15 elimination trials,including the U.S. State in which the trial was performed, the termitespecies tested, the Formulation tested, the amount consumed (number ofrods) and the number of days to elimination of the colony. In addition,comparisons to elimination data for Recruit IV are provided in FIGS. 29,30 and 31, in which FIG. 29 compares mean days to elimination betweenRecruit IV (RIV) and Formulation 16, FIG. 30 compares mean grams of baitconsumed to elimination between Recruit IV (RIV) and Formulation 16, andFIG. 31 compares mean grams of bait consumed to elimination adjusted forpercent AI in the AI-containing extruded composite matrix betweenRecruit IV (RIV) and Formulation 16.

TABLE 22 Trial Loca- Consumed Days to # tion Species Formul. (# of rods)elimination 1 FL R. flavipes Formulation 16 0.70 120 2 FL R. hageniFormulation 16 0.07 198 3 FL R. hageni Formulation 16 0.05 198 4 FL R.hageni Formulation 16 0.04 142 5 FL R. hageni Formulation 15 0.04 142 6FL R. hageni Formulation 15 0.30 198 7 FL R. hageni Formulation 16 0.06142 8 FL R. hageni Formulation 16 NA NA 9 FL R. hageni Formulation 160.05 120 10 LA C. formosanus Formulation 16 2.6  209 11 MS R. flavipesFormulation 16 0.31 166 12 MS R. flavipes Formulation 16 0.21 121 13 INR. flavipes Formulation 16 3.20 343 14 MS R. virginicus Formulation 160.05 121 15 CA R. Hesperus Formulation 16 0.01 121

The data set forth above show that the AI-containing extruded compositematerials did eliminate termite colonies. Average days to eliminationacross all trials was 188 and the maximum was 343, both within desiredparameters. The quantity of bait consumed averaged 0.37 rods with amaximum of 2.6 rods. Consumption of AI was roughly equivalent for R.flavipes and C. formosanus, but greatly reduced for other species. Thesetrials were initiated in late fall/winter, so the results are worstcase.

While multiple embodiments have been illustrated and described in detailin the drawings and foregoing description, the same is to be consideredillustrative and not restrictive in character, it being understood thatonly selected embodiments have been shown and described and that allchanges, equivalents, and modifications as would occur to those skilledin the art and that come within the scope of the inventions describedherein or defined by the following claims are desired to be protected.Any theory, mechanism of operation, proof, or finding stated herein ismeant to further enhance understanding of the present application and isnot intended to limit the inventions in any way to such theory,mechanism of operation, proof, or finding. In addition, the variousprocedures, techniques, and operations may be altered, rearranged,substituted, deleted, duplicated, or combined as would occur to thoseskilled in the art. Further, any U.S. patent, pending U.S. patentapplication Publication or other publication cited herein isincorporated herein by reference in its entirety as if each individualpublication, patent, or patent application was specifically andindividually indicated to be incorporated by reference and set forth inits entirety herein, including but not limited to, International PatentApplication Number PCT/US03/08690, filed 21 Mar. 2003, U.S. Pat. No.7,212,129 filed 21 Mar. 2002, U.S. Pat. No. 7,262,702 filed 9 Aug. 2001,International Patent Application Number PCT/US00/26373 filed 25 Sep.2000, International Patent Application Number PCT/US99/16519 filed 21Jul. 1999, U.S. Pat. No. 6,724,312 filed 25 Sep. 2000, and U.S.Published Patent Application No. 2001/0033230 filed 20 Mar. 2001. Inreading the claims, words such as the word “a,” the word “an,” the words“at least one,” and the words “at least a portion” are not intended tolimit the claims to only one item unless specifically stated to thecontrary. Further, when the language “at least a portion” and/or “aportion” is used, the claims may include a portion and/or the entireitem unless specifically stated to the contrary.

Any reference to a specific direction, for example, references to up,upper, down, lower, and the like, is to be understood for illustrativepurposes only or to better identify or distinguish various componentsfrom one another. Unless specifically identified to the contrary, allterms used herein are used to include their normal and customaryterminology. Further, while various embodiments of insect controldevices having specific components and structures are described andillustrated herein, it is to be understood that any selected embodimentcan include one or more of the specific components and/or structuresdescribed for another embodiment where possible.

What is claimed is:
 1. A method of delivering a pesticide to a pest,said method comprising the step of providing a pest control device tothe pest, wherein the pest control device comprises an extrudedcomposite material comprising i) a plastic structural matrix thatcomprises cellulose acetate butyrate (CAB), ii) a cellulosic foodmaterial that is palatable to the pest, and iii) a pesticide that istoxic to the pest, and wherein consumption of the extruded compositematerial by the pest delivers the pesticide to the pest.
 2. The methodof claim 1, wherein the method further comprises the step of installingthe pest control device in an area to be protected from the pest.
 3. Themethod of claim 1, wherein the pest control device further comprises apest sensor and a communication circuitry coupled to the pest sensor. 4.The method of claim 3, wherein the pest sensor includes a pest sensingcircuit.
 5. The method of claim 4, wherein the pest sensing circuitincludes an electrically conductive loop arranged to be altered duringconsumption or displacement of the cellulosic food material.
 6. Themethod of claim 1, wherein the electrically conductive loop is coupledto the communication circuitry to provide a two-state signal.
 7. Themethod of claim 6, wherein the two-state signal comprises a first stateof the signal corresponding to an electrically open condition of theloop and a second state of the signal corresponding to an electricallyclosed condition of the loop.
 8. The method of claim 1, wherein the CABis selected from the group consisting of CAB having a degree ofpolymerization from about 50 units to about 400 units, CAB having adegree of polymerization from about 100 units to about 300 units, CABhaving a degree of polymerization of about 160 units, and a combinationthereof.
 9. The method of claim 1, wherein the CAB comprises (a) amixture of CAB having from about 50 monomer units to about 75 monomerunits and CAB having from about 150 to about 300 monomer units, (b) amixture of CAB having about 60 monomer units and CAB having about 300monomer units, or (c) a mixture of CAB having about 64 monomer units andCAB having about 160 monomer units.
 10. The method of claim 1, whereinthe CAB comprises a mixture of CAB having a molecular weight of about16,000 and CAB having a molecular weight of about 40,000.
 11. The methodof claim 1, wherein the plastic structural matrix further comprises atleast one additional thermoplastic polymer.
 12. The method of claim 11,wherein the at least one additional thermoplastic polymer is selectedfrom the group consisting of cellulose acetate, cellulose acetatepropionate, polylactic acid, and a combination thereof.
 13. The methodof claim 1, wherein the plastic structural matrix comprises from about5% to about 50% by weight of the extruded composite material.
 14. Themethod of claim 1, wherein the cellulosic food material is selected fromthe group consisting of alpha cellulose, beta cellulose, gammacellulose, preferred texture cellulose (PTC), wood, wood chips, woodfibers, sawdust, cardboard, paper, microcrystalline cellulose, and acombination thereof.
 15. The method of claim 1, wherein the cellulosicfood material comprises a purified cellulose.
 16. The method of claim 1,wherein the pest is a cellulose-consuming organism.
 17. The method ofclaim 1, wherein the pest is a wood-destroying pest.
 18. The method ofclaim 1, wherein the pest is selected from the group consisting oftermites, carpenter ants, carpenter wasps, and a combination thereof.19. The method of claim 1, wherein the pest is a termite.
 20. The methodof claim 19, wherein the termite is a species selected from the groupconsisting of Reticulitermes flavipes, Coptotermes formosanus,Reticulitermes virginicus, Reticulitermes Hesperus, Reticulitermessperatus, and Heterotermes aureus.